Surface treatment method of aluminum material

Abstract

Disclosed is a method of treating a surface of an aluminum material, the method including: degreasing an aluminum material; etching the degreased aluminum material; performing a first desmutting treatment by immersing the etched aluminum material in a 25-35 wt % nitric acid solution at a temperature in a range of 25 to 30° C. for at least 60 seconds; performing a second desmutting treatment by immersing the first desmutting-treated aluminum material in a 5-15 wt % nitric acid solution at a temperature in a range of 25 to 30° C. for a time in a range of 30 seconds to 60 seconds; anodizing the second desmutting-treated aluminum material; coloring the anodized aluminum material; and sealing the colored aluminum material.