Additive for blended cement compositions, cement produced therefrom and methods related thereto
AssigneeCarbon Capture Machine (UK) Limited
InventorsMohammed S. Imbabi, Fredrik P. Glasser, Lewis McDonald
Life of this patent
Estimating the term…
Abstract
The present invention relates to a cement additive for use in a blended cement composition, the additive comprising a precipitated calcium carbonate formed from mineral sequestration of carbon dioxide.
Claims7
A method of changing the mineralogy of a blended cement composition, the method comprising:
- forming a precipitated calcium carbonate from mineral sequestration of carbon dioxide, the precipitated calcium carbonate being amorphous calcium carbonate or crystalline calcium carbonate having a particle size of 149 nm to 430 nm;
- introducing the amorphous calcium carbonate, or the crystalline calcium carbonate to the blended cement composition, the blended cement comprising Portland cement and the precipitated calcium carbonate being in the range 1 to 25 wt. % based on a total weight of the blended cement composition;
- raising a level of carbonate activity above a threshold necessary to form tilleyite and scawtite;
- wherein the raising the level of carbonate activity results in an intermediate activity between the threshold and the carbonate activity in which all hydrated cement phases of the group consisting of hemicarboaluminate, monocarbialuminate, ettringite, calcium silicate hydrate and Portanlandite are carbonated by exposing the blended cement composition to air;
- and
- forming tilleyite and scawtite in the blended cement composition at approximately 20 Celsius degree.
3 more elements
A method of changing the mineralogy of a blended cement composition, the method comprising:
- forming a precipitated calcium carbonate from mineral sequestration of carbon dioxide, the precipitated calcium carbonate being crystalline calcium carbonate having a D50 particle size of 6.3 microns;
- introducing the crystalline calcium carbonate to the blended cement composition, the blended cement comprising Portland cement and the precipitated calcium carbonate being in the range 1 to 25 wt. %, based on a total weight of the blended cement composition;
- raising a level of carbonate activity above a threshold necessary to form tilleyite and scawtite;
- wherein the raising the level of carbonate activity results in an intermediate activity between the threshold and the carbonate activity in which all hydrated cement phases of the group consisting of hemicarboaluminate, monocarbialuminate, ettringite, calcium silicate hydrate and Portanlandite are carbonated by exposing the blended cement composition to air;
- and
- forming tilleyite and scawtite at approximately 20 Celsius degree.
3 more elements
A method of changing the mineralogy of a blended cement composition, the method comprising:
- forming a precipitated calcium carbonate from mineral sequestration of carbon dioxide thereby producing amorphous calcium carbonate;
- introducing the amorphous calcium carbonate, to the blended cement composition, the blended cement composition comprising Portland cement and the precipitated calcium carbonate in the range 1 to 25 wt. % based on a total weight of the blended cement composition;
- raising a level of carbonate activity above a threshold necessary to form tilleyite and scawtite;
- wherein the raising the level of carbonate activity results in an intermediate activity between the threshold and the carbonate activity in which all hydrated cement phases of the group consisting of hemicarboaluminate, monocarbialuminate, ettringite, calcium silicate hydrate and Portanlandite are carbonated by exposing the blended cement composition to air;
- and
- forming tilleyite and scawtite at approximately 20 Celsius degree.
3 more elements
Dependencies are inferred from the claim text.