Method of forming a catalyst article on a substrate

Abstract

The present disclosure relates to a method for forming a catalyst article comprising: (a) forming a slurry having a solids content of up to 50 wt % by mixing together at least the following components a crystalline molecular sieve in an H+ or NH4+ form, an insoluble active metal precursor and an aqueous solvent at a temperature in the range 10 to 35° C.; (b) coating a substrate with the slurry formed in step (a); and (c) calcining the coated substrate formed in step (b) to form a catalyst layer on the substrate. The present disclosure further relates to a catalyst article, particularly a catalyst article which is suitable for use in the selective catalytic reduction of nitrogen oxides, and to an exhaust system.