Oxide layer-containing zirconium-niobium alloy ankle joint prosthetic system and manufacturing method

A preparation method of an ankle prosthesis containing zirconium-niobium alloy on an oxidation layer comprising the following steps:

• 1) using zirconium-niobium alloy powder as the raw material, conducting a 3D printing for one-piece molding, and obtaining a first intermediate of talus part and a first intermediate of tibial part respectively, putting the two first intermediates into the Sinter-HIP furnace, heating to 1250° C.-1400° C. under helium/argon gas protection, placing at a constant pressure of 140 MPa-180 MPa for 1 h to 3 h, reducing to a normal pressure, cooling to below 200° C. with the furnace, taking them out, and obtaining a second intermediate of talus part and a second intermediate of tibial part;
• 2) placing the second intermediate of the talus part and the second intermediate of the tibial part in a programmable thermostat to cool to −80° C. to −120° C. at a rate of 1° C./min, keeping them at a constant temperature for 5 h to 10 h, and taking them out of the programmed thermostat;
• placing them in a liquid nitrogen for 16 h to 36 h, and adjusting the temperature to a room temperature so as to obtain a third intermediate of talus part and a third intermediate of tibial part;
• 3) placing the third intermediate of the talus part and the third intermediate of the tibial part in a programmable thermostat to cool to −80° C. to −120° C. at a rate of 1° C./min, and placing them at a constant temperature for 5 h to 10 h, taking them out of the programmed thermostat, placing them in the liquid nitrogen for 16 h to 36 h and adjusting the temperature to room temperature so as to obtain a fourth intermediate of talus part and a fourth intermediate of tibial part;
• 4) machining, finishing, polishing, cleaning, and drying the fourth intermediate products fourth intermediate of the talus part and the fourth intermediate of the tibial part, and obtaining a fifth intermediate of talus part and a fifth intermediate of tibial part;
• the roughness of the upper surface of the fifth intermediate product of the talus part and the lower surface of the fifth intermediate product of the tibial part is Ra≤0.050 μm;
• 5) placing the fifth intermediate of the talus part and the fifth intermediate of the tibial part in a tube furnace, introducing normal-pressure helium/argon gas containing 5% to 15% of oxygen in percentage by mass, heating to 500° C. to 700° C. at 5° C./min to 20° C./min, and cooling down to 400° C. to 495° C. at 0.4° C./min to 0.9° C./min;
• and cooling to be below 200° C. sequentially, taking them out to obtain the talus part and tibial part;
• the structure of the talus part is the same as its first intermediate, second intermediate, third intermediate, fourth intermediate and fifth intermediate;
• the structure of the tibial part is the same as its first intermediate, second intermediate, third intermediate, fourth intermediate, and fifth intermediate;
• the ankle prosthesis containing zirconium-niobium alloy on the oxidation layer comprises a talus part (1) and a tibial part (2), the talus part (1) comprises a talus body (4) and two first fixations (3) arranged at the front and rear direction of the lower surface of the talus body (4);
• the tibial part (2) comprises a tibial body (5) and two second fixations (6) arranged at the front and rear direction of the upper surface of the tibial body (5);
• the talus part (1) is connected with the tibial part (2) in a sliding mode;
• a bone trabeculae (7) is arranged on the lower surface of the talus body (4) and the outer surfaces of the two first fixations (3), and the bone trabeculae (7) is arranged on the upper surface of the tibial body (5) and the outer surfaces of the two second fixations (6) as well, the pore size of the bone trabeculae (7) ranges from 0.35 mm-1.10 mm, the porosity ranges from 55% to 78%, through-hole ratio is 100%, and the thickness ranges from 0.5 mm-3 mm.