Aqueous methods for titanating a chromium/silica catalyst with an alkali metal

Abstract

Methods for making titanated silica supports, titanated chromium/silica pre-catalysts, and activated titanated chromium/silica catalysts are disclosed in which hydrogen peroxide and an alkali metal precursor are used during catalyst preparation. Resulting titanated chromium/silica pre-catalysts often contain silica, 0.1 to 5 wt. % chromium, 0.1 to 10 wt. % titanium, and less than or equal to 4 wt. % carbon, and further contain an alkali metal or zinc at a molar ratio of alkali metal:titanium or zinc:titanium from 0.02:1 to 3:1 and/or at an amount in a range from 0.01 to 2 mmol of alkali metal or zinc per gram of the silica. High melt index potential activated titanated chromium/silica catalysts can be used to polymerize olefins to produce, for example, ethylene based homopolymers and copolymers having HLMI values of greater than 30 g/10 min.