Method of making negative electrode material

Abstract

A method of making negative electrode material having silicon and silicate includes the steps of providing raw materials for contact fusion, heating the raw materials to form materials with a contact-fusion state, mixing silicon and the materials after forming contact-fusion to form a composite material, and vaporizing the composite materials on the deposition zone after the mixing step. The heating step is performed at the temperatures between the lowest melting temperature of the materials with the contact-fusion state and 1400° C. The deposited composite materials can be optionally heat treated, pulverized, and/or coated with carbon. Also provided is a negative electrode material of silicon and silicate made from the steps described above. The negative electrode material of silicon and silicate can be an Li—Mg silicate having silicon powder dispersed therein, the Li—Mg silicate forming a uniform interface on surfaces of the silicon powder.