Tearable tube formed from fluororesin

A method for producing a fluororesin tube, the method comprising:

• (a) a step of subjecting a thermoplastic fluororesin to melt extrusion molding through an extrusion molding machine at a temperature of about 260 to 450° C., wherein a temperature at which the thermoplastic fluororesin is melted and formed into a tubular shape is about 260 to 450° C., wherein the thermoplastic fluororesin is selected from the group consisting of a tetrafluoroethylene-hexafluoropropylene copolymer and a tetrafluoroethylene-perfluoroalkyl vinyl ether copolymer, wherein in the melt extrusion molding, the extrusion molding machine is configured so that a flow path of the molten thermoplastic fluororesin passing through the extrusion molding machine is temporarily branched to form a weld line in a lengthwise direction in the fluororesin tube, wherein the extrusion molding machine is configured so that the branched thermoplastic resin merges while the thermoplastic resin is contained within the extrusion molding machine and wherein the weld line of the fluororesin tube is not visible and does not have any crack associated with the weld line, and
• (b) a step of expanding an inner diameter of the fluororesin tube by applying a pressure from the inside of the fluororesin tube while heating the fluororesin tube with the weld line,
• wherein the fluororesin tube is transparent and wherein a tear strength of the fluororesin tube is less than 8.0 N/mm, and
• wherein a leg portion is provided in the extrusion molding machine in the flow path of the molten thermoplastic fluororesin and wherein a distance between an outlet of the extrusion molding machine and the leg portion is at least 10 mm.