Abstract

Disclosed are a composite resin denture porcelain block, a preparation method thereof and a composite resin denture. The composite resin denture porcelain block includes 0.1% to 15% of carbamate dimethacrylate, 0.1% to 10% of bisphenol A-di glycidyl methacrylate, 3% to 20% of triethylene glycol dimethacrylate, 35% to 85% of glass powder, 0.1% to 8% of ZrO2, 3% to 15% of SiO2, 0.1% to 40% of ZrO2—SiO2 composite powder, 2% to 17% of diatomite, 0.01% to 3% of benzoyl peroxide, 0.01% to 3% of N,N dihydroxyethyl p-toluidine, 0.01% to 3% of 2,6 di-tert-butyl p-cresol, 0.001% to 0.2% of iron oxide red, 0.001% to 0.2% of iron oxide black, and 0.001% to 0.5% of iron oxide yellow. The composite resin denture porcelain block of the present application uses carbamate dimethacrylate, bisphenol A-di glycidyl methacrylate, and triethylene glycol dimethacrylate as the resin matrix.