Abstract

Provided is the use of a silane composite emulsion as an anti-cracking enhancer in a cement-based material. In the present disclosure, active groups on an isobutyltriethoxysilane molecule react with hydroxyl groups on a surface of a mortar to form a layered hydrophobic structure, slowing down a water loss inside the mortar of a cement-based material. The dehydration of butyl acrylate forms a network structure, which fills pores of the cement-based material, inhibits shrinkage of the cement-based material, and reduces the cracking caused by the shrinkage. Tetraethoxysilane can undergo hydrolysis at a room temperature to generate nano-silica with a large number of hydroxyl groups on a surface; and the nano-silica can undergo secondary hydration with calcium hydroxide in the cement to form a secondary hydration product C—S—H gel, thereby filling most of voids to make a structure of the cement hydration product denser, to increase a strength of the mortar.