Die-casting metal part-polymer resin composite and method for preparing same
AssigneePlastal SPA
InventorsMu Chang Sung, Jae Ik Kim, Jae Hwa Kim, Sung Ho Hong
Life of this patent
Estimating the term…
Abstract
The present invention relates to a metal-polymer resin composite in which a polymer resin is directly injection-molded to a zinc alloy, a magnesium alloy, or a die-casting part thereof, and thus an injection product is directly bonded to a metal surface, wherein in the case of a hard polymer resin, a tensile strength of the metal and the polymer resin is 30 MPa or greater, and in the case of a soft polymer resin, a tensile strength of the metal and the polymer resin is 20 MPa or greater, and an average helium leakage after 10 times of measurement is 10−8 Pa·m3/s or less, and a novel method for preparing the same.
Claims4
A method for preparing a metal-polymer resin composite by bonding a metal member, which is a zinc alloy, a magnesium alloy, or a die-casting part thereof, to a polymer resin through a degreasing process, an etching process, an electrolysis process, and an injection process,
- wherein the metal member is subjected to etching, desmutting, and ultrasonic cleaning,
- the electrolysis process is performed in an electrolyte containing at least one of (1) a hydroxide of an alkali metal or an alkaline earth metal, (2) a phosphate compound or a sulfate compound, and (3) a silicate compound,
- the hydroxide of an alkali metal or an alkaline earth metal is at least any one of sodium hydroxide, potassium hydroxide, magnesium hydroxide, or calcium hydroxide,
- the phosphate compound is at least any one of sodium pyrophosphate, sodium acid pyrophosphate, calcium pyrophosphate, tin pyrophosphate, copper pyrophosphate, iron pyrophosphate, sodium iron pyrophosphate, potassium pyrophosphate, isopentenyl pyrophosphate, melamine pyrophosphate, or thiamine pyrophosphate,
- the sulfate compound is at least any one of ammonium sulfate, ammonium persulfate, ammonium hydrogen sulfate, calcium sulfate, potassium persulfate, potassium pyrosulfate, zinc sulfate, sodium thiosulfate, sodium hydrogen sulfate, sodium sulfate, sodium pyrosulfate, kanamycin sulfate, cerium sulfate, cefquinome sulfate, sodium dodecyl sulfate, or magnesium sulfate,
- the hydroxide of an alkali metal or an alkaline earth metal is in an amount of 0.1 to 20 parts by weight with respect to 100 parts by weight of distilled water,
- the sulfate compound is in an amount of 0.1 to 20 parts by weight with respect to 100 parts by weight of distilled water,
- the silicate compound is in an amount of 0.1 to 30 parts by weight with respect to 100 parts by weight of distilled water, and
- when two or more materials are used together in the electrolysis process, the materials are in a relative amount of 40 to 350 parts by weight of phosphate and 30 to 150 parts by weight of silicate with respect to 100 parts by weight of the hydroxide of an alkali metal or an alkaline earth metal.
Dependencies are inferred from the claim text.