Polyolefin resin composition for porous film

Abstract

Disclosed are a polyolefin resin composition usable in manufacturing a single-layered dry porous membrane having excellent meltdown and shutdown properties, and a porous membrane using the polyolefin resin composition. The present invention provides a polyolefin resin composition for a porous membrane, wherein the polyolefin resin composition includes 30 wt % to 70 wt % of a high-density polyethylene having a melt flow index (190° C., 2.16 kg load) of 0.1 g/10 min to 5 g/10 min, a crystallization temperature of 115° C. to 125° C., and a degree of crystallinity of 75% or greater, and 30 wt % to 70 wt % of a high-crystallinity polypropylene having a melt flow index (230° C., 2.16 kg load) of 5 g/10 min to 20 g/10 min.