Zonal trabecular uni-compartmental femoral condylar component containing zirconium-niobium alloy on oxidation layer and preparation method thereof

A preparation method of a zonal trabecular uni-compartmental femoral condylar component containing zirconium-niobium alloy with an oxidation layer, the method comprising the following steps:

• 1) Using zirconium-niobium alloy powder as a raw material, conducting a 3D printing for one-piece molding, and obtaining a first intermediate product of the zonal trabecular uni-compartmental femoral condylar component containing zirconium-niobium alloy with the oxidation layer, putting the first intermediate product into a Sinter-HIP furnace, heating to 1250° C. under helium/argon gas protection, and placing at a constant pressure of 180 MPa for 3 h, and reducing to an atmospheric pressure, cooling to below 200° C. with the furnace, taking it out, and obtaining a second intermediate product;
• 2) Putting the second intermediate product into a programmable thermostat, cooling to −80° C. at a rate of 1° C./min, keeping the second intermediate product at a constant temperature of −80° C. for 10 h, and taking the second intermediate product out of the programmable thermostat;
• and putting it into a liquid nitrogen for 16 h, and adjusting the temperature to room temperature so as to obtain a third intermediate product;
• 3) Putting the third intermediate product in the programmable thermostat, cooling to −80° C. at a rate of 1° C./min, and placing the third intermediate product at a constant temperature of −80° C. for 10 h, taking the third intermediate product out of the programmable thermostat, and putting the third intermediate product into the liquid nitrogen for 16 h, and adjusting the temperature to room temperature so as to obtain a fourth intermediate product;
• 4) Machining, finishing, polishing, cleaning, and drying the fourth intermediate product, and obtaining a fifth intermediate product, where an upper surface roughness of an articular surface of the fifth intermediate product is Ra=0.12 μm;
• 5) Putting the fifth intermediate product into a tube furnace, introducing an atmospheric pressure helium/argon gas containing 5% oxygen in percentage by mass, heating to 500° C. at 5° C./min, and cooling to 400° C. at 0.4° C./min, and cooling to be below 200° C. sequentially, take the fifth intermediate product out to obtain the zonal trabecular uni-compartmental femoral condylar component containing zirconium-niobium alloy with the oxidation layer;
• the structure of the zonal trabecular uni-compartmental femoral condylar component containing zirconium-niobium alloy with the oxidation layer is same as the structure of the first intermediate product, the second intermediate product, the third intermediate product, the fourth intermediate product and the fifth intermediate product;
• the zonal trabecular uni-compartmental femoral condylar component containing zirconium-niobium alloy with the oxidation layer includes an articular surface (1) and an osseointegration surface (2), a longitudinal section of the articular surface (1) is arc-shaped, the osseointegration surface (2) comprises a rear osseointegration surface (21) and a distal osseointegration surface (22), the rear osseointegration surface (21) is arranged in a vertical plane, the distal osseointegration surface (22) is arc-shaped which has a common spherical center with the articular surface (1);
• a first cylindrical fixation (4) is arranged in the middle of the distal osseointegration surface (22), a second cylindrical fixation (5) is arranged at the front of the distal osseointegration surface (22);
• and the diameter of the second cylindrical fixation 5 is smaller than that of the first cylindrical fixation (4);
• a side wall (3) is arranged at the edge of the osseointegration surface (2), a bone trabeculae 6 is arranged in the side wall (3) except the location where connecting the first cylindrical fixation (4) and the second cylindrical fixation (5);
• a bone trabecular partition line (7) is positioned in the middle of the front and rear direction of the osseointegration surface (2);
• a first bone trabeculae (8) and a second bone trabeculae (9) are respectively arranged before and after the bone trabecular partition line (7);
• and the pore size and porosity of the first bone trabeculae (8) is smaller than those of the second bone trabeculae (9).