Loading patent…
AssigneeJf Polymers (Suzhou) Co., Ltd.
InventorsXiaofan Luo, Zhaokun Pei
Estimating the term…
Provided is a new and better solution to the problems associated with the premature softening of PLA filaments in the additive manufacturing of three dimensional articles. It is based upon the finding that poly (lactic acid) filaments with high crystallinity offer much better resistance to heat-induced softening. The crystalline poly (lactic acid) filament can accordingly be used in the additive manufacturing of three dimensional articles without encountering the problems associated with premature softening, such as poor quality and printer jamming. The crystalline poly (lactic acid) filaments can also be used in additive manufacturing of three dimensional articles without compromising the quality of the ultimate product, reducing printing speed, increasing cost, or leading to increased printer complexity. It more specifically discloses a filament for use in three-dimensional printing which is comprised of crystalized poly (lactic acid), wherein said filament has a diameter which is within the range of 1.65 mm to 1.85 mm.
A filament for use as a feedstock in three-dimensional printing, said filament being a solid filament which consists of crystalized poly(lactic acid), optionally, one or more nucleating agents, optionally, one or more colorants, optionally, one or more pigments, optionally, one or more fillers, optionally, one or more plasticizers, optionally, one or more heat/IV stabilizers, and optionally, one or more impact modifiers, wherein said crystalized poly(lactic acid) has a degree of crystallinity which is within the range of 10 percent to 40 percent, wherein said filament has a diameter which is within the range of 1.65 mm to 1.85 mm or which is within the range of 2.75 mm to 3.15 mm, wherein said filament is capable of passing through a ring gauge having an internal diameter which is 0.15 mm larger than the average diameter of the filament at a speed of 50 meters/minute without breaking, and wherein the crystalized poly(lactic acid) has a d-lactic acid content which does not exceed 15% percent, and wherein the filament is on a spool.
A filament for use as a feedstock in three-dimensional printing, said filament being a solid filament which consists of crystalized poly(lactic acid), optionally, one or more nucleating agents, optionally, one or more colorants, optionally, one or more pigments, optionally, one or more fillers, optionally, one or more plasticizers, optionally, one or more heat/IV stabilizers, and optionally, one or more impact modifiers, wherein said crystalized poly(lactic acid) has a degree of crystallinity which is within the range of 10 percent to 40 percent, wherein said filament has a diameter which is within the range of 1.65 mm to 1.85 mm or which is within the range of 2.75 mm to 3.15 mm, wherein the filament is adapted for use in fused filament fabrication additive manufacturing, wherein said filament is capable of passing through a ring gauge having an internal diameter which is 0.15 mm larger than the average diameter of the filament at a speed of 50 meters/minute without breaking, and wherein the crystalized poly(lactic acid) has an l-lactic acid content which is within the range of 85 percent to 100 percent, and wherein the filament is adapted for use in fused deposition modeling and is on a spool.
Dependencies are inferred from the claim text.