Method for producing a pipe fitting, in particular by weld overlay
AssigneeLinde Aktiengesellschaft
InventorGeorg Wimmer
Life of this patent
Estimating the term…
Abstract
The invention relates to a process for producing a pipe fitting (10), for example a reduction piece, a pipe elbow or a branch, wherein a metallic material (11) is melted by heating, and wherein a plurality of material layers (12) is produced in a successive manner from the melted material (11), wherein the in each case produced material layer (12) is materially bonded to the in each case previous material layer (12), and wherein the pipe fitting (10) is formed from the material layers (12) bonded to one another. The pipe fitting (10) is produced by buildup welding, for example arc welding or beam welding.
Claims8
A process for producing a pipe fitting comprising:
- producing a first material layer by melting a metallic material by heating, wherein the metallic material is melted by means of heat generated by an electric arc, said electric arc being formed by applying an electrical voltage between a welding electrode and a counter electrode, and
- producing a plurality of further material layers in a successive manner on to said first material layer, in each case by melting metallic material,
- wherein each produced material layer, after said first material layer, is materially bonded to the previous material layer by means of the heat generated by the electric arc, wherein the welding electrode is formed from the metallic material, and at least one electrode section of the welding electrode is melted by means of the heat generated by the electric arc, and the material layers are each formed from the melted electrode section of the welding electrode,
- wherein the metallic material is an aluminum alloy with a proportion by weight of magnesium of at least 2.5%,
- wherein the metallic material is provided in the form of a wire and the welding electrode is formed from the wire, and
- wherein at least one wire section of the wire is melted by the heating, and the material layers are formed from the melted wire section of the wire to result in the pipe fitting which remains dimensionally stable to a fluid guided through the interior space of the pipe at at least an internal pressure of 10 bar.