Metal electrode of ceramic capacitor and method of forming the same

A method of forming a metal electrode of a ceramic capacitor, comprising:

• mixing metal powders, a metal oxide organic-precursor and a barium titanate organic-precursor to obtain precursor powders, wherein based on an amount of the metal powders as 100 wt %, an amount of the barium titanate organic-precursor is 3 wt % to 15 wt %, and based on an amount of the barium titanate organic-precursor as 100 mol %, an amount of the metal oxide organic-precursor is 0.5 mol % to 5 mol %;
• adding an adhesive to the precursor powders to obtain a metal slurry;
• performing a molding process to the metal slurry to obtain a film material;
• performing a binder burn-out process to the film material to obtain a degumming film, wherein the binder burn-out process makes the barium titanate organic-precursor transform to barium titanate;
• and
• performing a sintering process to the degumming film to obtain the metal electrode.