Method of manufacturing antifouling coating polymer using initiated chemical vapor deposition
AssigneeIndustry-Academic Cooperation Foundation, Chosun University
InventorsJae Bok Kwak, Chang Hoon Kim, Jeong Heon Lee
Life of this patent
Estimating the term…
Abstract
A method of manufacturing an antifouling coating layer is disclosed. The method includes depositing a fluorine-based monomer, a crosslinking agent, and an initiator on a substrate by putting them into an iCVD chamber. The fluorine-based monomer is one, or two or more selected from a group of C2FMA, C3FMA, C4FMA, C5FMA, C6FMA, C7FMA, and C8FMA. The antifouling coating layer has excellent antifouling characteristic and durability through quick deposition using iCVD.
Claims2
A method of manufacturing an antifouling coating layer, the method comprising depositing a fluorine-based monomer, a crosslinking agent, and an initiator on a substrate by putting them into an iCVD chamber,
- wherein the fluorine-based monomer is one or two selected from a group of C7FMA and C8FMA,
- wherein a flow rate ratio of the fluorine-based monomer, the crosslinking agent, and the initiator that are put into an iCVD chamber is fluorine-based monomer:crosslinking agent:initiator=2:0.7-1.5:1,
- wherein the crosslinking agent is GMA (glycidyl methacrylate),
- wherein the initiator is TBPO (tert-butyl peroxide),
- wherein the fluorine-based monomer is heated at 60 to 90° C.,
- wherein the crosslinking agent is heated at 30 to 45° C.,
- wherein a flow rate of the fluorine-based monomer is 8.4 to 10.4 (standard cubic centimeter per minute) sccm,
- wherein a flow rate of the crosslinking agent is 3.5 to 8 sccm,
- wherein a flow rate of the initiator is 4.6 to 5.4 sccm, and
- wherein the substrate is an ITO (Indium Tin Oxide) transparent electrode.
A method of manufacturing an antifouling coating layer, the method comprising depositing a fluorine-based monomer, a crosslinking agent, and an initiator on a substrate by putting them into an iCVD chamber,
- wherein the fluorine-based monomer is one or two selected from a group of C7FMA and C8FMA,
- wherein a flow rate ratio of the fluorine-based monomer, the crosslinking agent, and the initiator that are put into an iCVD chamber is fluorine-based monomer:crosslinking agent:initiator=2:0.7-1.5:1,
- wherein the crosslinking agent is GMA (glycidyl methacrylate),
- wherein the initiator is TBPO (tert-butyl peroxide),
- wherein the fluorine-based monomer is heated at 60 to 90° C.,
- wherein the crosslinking agent is heated at 30 to 45° C.,
- wherein a flow rate of the fluorine-based monomer is 8.4 to 10.4 (standard cubic centimeter per minute) sccm,
- wherein a flow rate of the crosslinking agent is 3.5 to 8 sccm,
- wherein a flow rate of the initiator is 4.6 to 5.4 sccm, and
- wherein the substrate is a silver nano wire (AgNW) transparent electrode.
Dependencies are inferred from the claim text.