Carbon black from biomass
AssigneeNorse Biotech AS
InventorRay W Chrisman
Life of this patent
Estimating the term…
Abstract
A process for making carbon black is described by pyrolizing unsulfonated lignin or by pyrolizing aromatic monomers formed by hydrolyzing a biomass comprising unsulfonated lignin.
Claims10
A process for making carbon black comprising a furnace black process wherein biomass is first separated into component biopolymers of cellulose, hemicellulose, and lignin, and then hydrolyzing the lignin polymers to form unsulfonated aromatic lignin monomers which replace aromatics from hydrocarbon refineries as feed stock for the process.
A process for making carbon black by:
- (a) exposing biomass comprising natural lignin to pressurized water heated to a temperature above 100° C. to depolymerize the lignin to comprise aromatic monomers of coumaryl alcohol, coniferyl alcohol, and/or sinapyl alcohol;
- and (b) pyrolyzing the aromatic monomers to form carbon black.
A process for preparing carbon black from biomass which comprises:
- a. separating a natural lignin polymer from the biomass by solubilizing with pressurized water at a temperature of about 160° C.;
- b. separating hemicellulose from the biomass of step a, which is converted to hemicellulose monomers from solids of the biomass;
- c. heating solids from step b to a higher temperature to liquefy the residual lignin polymer solids while still not dissolving cellulose present in the residual ligand polymer solids;
- d. separating the liquefied lignin polymer of step c from the biomass to retain the cellulose;
- e. maintaining the liquified lignin polymer of step d in pressurized water at a temperature of about 170° C. for a sufficient time to hydrolyze the liquified lignin to lignin monomers;
- f. flashing off the water from step e and drying the lignin monomers;
- and
- g. feeding the dried monomers from step f into a high temperature reactor to form the carbon black.
A process for making carbon black comprising a furnace black process wherein biomass is first separated into component biopolymers of cellulose, hemicellulose, and lignin, and then hydrolyzing the lignin polymers to form unsulfonated aromatic lignin monomers, wherein the unsulfonated aromatic lignin monomers are derived from unsulfonated lignin obtained from a Kraft process or black liquor, after removing the sulfur from the lignin, which unsulfonated aromatic lignin monomers are feed stock for the process.