Back to results
US 12,331,261 B2Granted
Composition and method of manufacturing sulfonate-based greases using a glycerol derivative
AssigneeNCH Corporation
InventorsJ. Andrew Waynick, Gaston Aguilar
Life of this patent
Estimating the term…
Abstract
A sulfonate-based grease composition and method of manufacture comprising the addition of one or more glycerol derivatives. The glycerol derivative acts to optimally disperse the thickener in the grease such that the conventional step of milling the grease may not be needed. The glycerol derivative reacts with water to form in-situ complexing acids, which may replace at least some of the normally used complexing acids for reacting with calcium containing bases. The greases according to preferred embodiments have a high dropping point, improved thickener yield, and faster conversion time.
Claims43
A method for making a complex sulfonate-based grease comprising the steps of:
- adding and mixing (1) 33% or less overbased calcium sulfonate having amorphous calcium carbonate dispersed therein and (2) water;
- adding and mixing 0.1 to 5% of one or more conventional non-aqueous converting agents after a converting agent delay period comprising (1) a converting agent holding delay period wherein a mixture comprising the overbased calcium sulfonate and the water is maintained at a temperature or within a range of temperatures for a period of time of at least 20 minutes or (2) a converting agent temperature adjustment delay period where the mixture comprising the overbased calcium sulfonate and the water is heated or (3) a combination thereof;
- converting a mixture comprising the overbased calcium sulfonate, the water, and the one or more conventional non-aqueous converting agents by heating until conversion of the amorphous calcium carbonate contained in the overbased calcium sulfonate to a crystalline form has occurred;
- adding and mixing 1.25 to 18% total of one or more complexing acids prior to the converting step, during the converting step, or after the converting step;
- adding and mixing 1 to 20% total of one or more calcium containing bases prior to the converting step, during the converting step, or after the converting step;
- and
- adding and mixing 0.1 to 6% of a glycerol derivative after the converting step, wherein the addition of the glycerol derivative forms an acid reaction product from hydrolyzing the glycerol derivative, wherein no glycerol derivative is added prior to the converting step, and wherein the glycerol derivative comprises (1) glycerol mono-oleate, (2) hydrogenated castor oil, (3) glycerol mono-stearate, (4) glycerol mono-tallowate, or (5) a combination thereof;
- adding and mixing an alkali metal hydroxide after the converting step, wherein no alkali metal hydroxide is added prior to the converting step;
- heating to a temperature sufficient to remove the water;
- wherein the percentages are by weight.
7 more elements
A method for making a complex sulfonate-based grease comprising the steps of:
- adding and mixing (1) 33% or less overbased calcium sulfonate having amorphous calcium carbonate dispersed therein and (2) water;
- adding and mixing 0.1 to 5% of one or more conventional non-aqueous converting agents after a converting agent delay period, wherein the one or more conventional non-aqueous converting agents comprise an alcohol, ether, glycol, glycol ether, glycol polyether, or combinations thereof and wherein the converting agent delay period comprises (1) a converting agent holding delay period wherein a mixture comprising the overbased calcium sulfonate and the water is maintained at a temperature or within a range of temperatures for a period of time of at least 20 minutes or (2) a converting agent temperature adjustment delay period where the mixture comprising the overbased calcium sulfonate and the water is heated or (3) a combination thereof;
- converting a mixture comprising the overbased calcium sulfonate, the water, and the one or more conventional non-aqueous converting agents by heating until conversion of the amorphous calcium carbonate contained in the overbased calcium sulfonate to a crystalline form has occurred;
- adding and mixing 1.25 to 18% total of one or more complexing acids, wherein the one or more complexing acids comprise 12-hydroxystearic acid, acetic acid, phosphoric acid, and boric acid;
- adding and mixing 1 to 20% total of one or more calcium containing bases prior to the converting step, during the converting step, or after the converting step, wherein the one or more calcium containing bases comprise calcium hydroxyapatite, added calcium carbonate, added calcium hydroxide, or a combination thereof;
- adding and mixing an alkali metal hydroxide after the converting step, wherein no alkali metal hydroxide is added prior to the converting step;
- adding and mixing 0.1 to 1.0% of a glycerol derivative after the adding and mixing the alkali metal hydroxide step, wherein the addition of the glycerol derivative forms an acid reaction product from hydrolyzing the glycerol derivative, wherein no glycerol derivative is added prior to the converting step, and wherein the glycerol derivative comprises hydrogenated castor oil;
- adding and mixing a facilitating acid prior to the converting step;
- and
- heating to a temperature sufficient to remove the water;
- wherein a first portion of the 12-hydroxystearic acid and a first portion of the acetic acid are added prior to or during the converting step;
- and
- wherein a second portion of the 12-hydroxystearic, a second portion of the acetic acid, all of the phosphoric acid, and all of the boric acid are added after the adding and mixing the glycerol derivative step;
- wherein none of the one or more complexing acids are added between completion of the converting step and the adding and mixing the glycerol derivative step;
- wherein the calcium hydroxyapatite, a first portion of the added calcium carbonate, and a first portion of the added calcium hydroxide are added prior to the converting step;
- wherein a second portion of the added calcium carbonate and a second portion of the added calcium hydroxide are added after the converting step;
- wherein no overbased magnesium sulfonate is added;
- and
- wherein the percentages are by weight.
16 more elements
A method for making a complex sulfonate-based grease comprising the steps of:
- adding and mixing (1) 33% or less overbased calcium sulfonate having amorphous calcium carbonate dispersed therein and a Total Bae Number of 400 or higher, and (2) water;
- adding and mixing 0.1 to 5% of one or more conventional non-aqueous converting agents after a converting agent delay period comprising (1) a converting agent holding delay period wherein a mixture comprising the overbased calcium sulfonate and the water is maintained at a temperature or within a range of temperatures for a period of time of at least 20 minutes or (2) a converting agent temperature adjustment delay period where the mixture comprising the overbased calcium sulfonate and the water is heated or (3) a combination thereof;
- converting a mixture comprising the overbased calcium sulfonate, the water, and the one or more conventional non-aqueous converting agents by heating until conversion of the amorphous calcium carbonate contained in the overbased calcium sulfonate to a crystalline form has occurred;
- adding and mixing 1.25 to 18% total of one or more complexing acids comprising 12-hystoxystearic acid prior to the converting step, during the converting step, or after the converting step;
- adding and mixing 1 to 20% total of one or more calcium containing bases prior to the converting step, during the converting step, or after the converting step;
- heating to a temperature sufficient to remove the water;
- and
- adding and mixing 0.1 to 1.0% of a glycerol derivative prior to the heating to a temperature sufficient to remove the water step, wherein the addition of the glycerol derivative forms an acid reaction product from hydrolyzing the glycerol derivative with the water, and wherein the glycerol derivative comprises hydrogenated castor oil;
- and
- wherein the percentages are by weight.
7 more elements
Dependencies are inferred from the claim text.