Polymerisation of siloxane polymers

A silanol-terminated silicone polymer gum production process, wherein the silanol-terminated silicone polymer gum has a William's plasticity of at least 200 mm/100 in accordance with ASTM D-926-08;

• the silanol-terminated silicone polymer gum production process comprising:
• undertaking a ring opening polymerization of one or more organocyclosiloxane oligomer(s) having from 3 to 5 siloxane units per molecule, which siloxane units comprise dialkylsiloxane units, alkylalkenylsiloxane units, trifluoroalkyl alkylsiloxane units, perfluoroalkyl alkyl siloxane units, phenylalkyl alkylsiloxane units or mixtures thereof in the organocyclosiloxane ring, wherein each alkyl group is the same or different and contains from 1 to 10 carbons, each alkenyl group is the same or different and has from 2 to 10 carbons;
• by
• (i) transporting the one or more organocyclosiloxane oligomer(s) having from 3 to 5 siloxane units per molecule to a polymerisation reactor, which polymerisation reactor is heated to a pre-defined temperature of from 40 to 170° C. in an inert atmosphere;
• (ii) simultaneously with or subsequent to step (i), introducing a suitable —OH species containing chain initiator/endblocker into the polymerisation reactor and mixing same with the organocyclosiloxane oligomer(s) while residual water is removed, if required;
• (iii) introducing a catalyst, suitable for catalysing the ring opening polymerization, into the polymerisation reactor to form a reaction mixture with the resulting mixture of step (ii) and subsequently proceeding with ring opening polymerisation of the at least one organocyclosiloxane oligomer(s) to generate a silicone polymer gum reaction product;
• (iv) quenching the silicone polymer gum reaction product resulting from step (iii) and optionally vacuum stripping the silicone polymer gum reaction product with a vacuum means in the polymerisation reactor;
• (v) cooling the silicone polymer gum reaction product resulting from step (iv) to form a final silicone polymer gum reaction product;
• and then undertaking either one of steps (vi) or (vii) or both of steps (vi) and (vii);
• (vi) transporting the final silicone polymer gum reaction product to a packaging means (30) for packaging in a suitable storage container;
• (vii) transporting the final silicone polymer gum reaction product to a compounding means for combining the silicone polymer gum reaction product with other ingredients;
• wherein the polymerisation reactor utilised is a conical screw dump extruder (1) comprising a conical twin screw chamber (1a), the conical twin screw chamber (1a) housing two counter-rotating conical screws converging towards an extrusion die (2) having an entrance and an exit wherein passage through the extrusion die (2) is controlled by an occlusion means (3) such that the exit of the extrusion die (2) is adapted to be closed by the occlusion means (3) up to the end of step (v) and be open during steps (vi), step (vii) or both of steps (vi) and (vii) such that during polymerisation the reaction mixture is driven towards extrusion die (2) by the pair of counter-rotating conical screws, and then forced to go back into the conical twin screw chamber (1a) when the extrusion die (2) is closed by the occlusion means (3) and then during steps (vi), step (vii) or both of steps (vi) and (vii) is extruded through the extrusion die (2) and transported to the packaging means (30) and/or compounding means respectively.