Process for producing clean steel products with a low nitrogen content using an electric arc furnace and a degassing system

Abstract

A process for producing clean steel products with low nitrogen content, below 35 ppm, in a steelmaking plant comprising a direct reduced iron (DRI) source, which may be a direct reduction plant or a DRI storage facility, an electric arc furnace (EAF), a vacuum degassing system (DS), and a continuous casting system (CC) is disclosed. The process comprises a first stage of melting and refining a metallic iron charge, a second stage of tapping molten steel from the electric arc furnace (EAF) into a ladle, a third stage of exposing molten steel to a pressure below the atmospheric pressure and a fourth stage of casting molten steel to clean steel products. Optionally, the molten steel tapped from the EAF is treated in a ladle furnace (LF) prior to being treated in the degassing system (DS). The metallic iron charge fed to the EAF comprises more than 70% by weight of DRI in the form of pellets or briquettes having a carbon content above 2.5 weight %. Preferably, the metallic iron charge is fed to the EAF at a temperature of 400° C. or higher. The low nitrogen level in the steel products made according to the Application is achieved by forming a first foamy slag in said first process stage and is maintained in a foamy state by controlling the feed of fluxes, oxygen, and carbonaceous materials to the EAF and by forming a second slag, after molten steel is tapped from the EAF, having a predetermined composition capable of continuing the desulfurization and providing a thermal and chemical insulation to prevent nitrogen pickup and promote nitrogen removal of molten steel. The process also comprises carrying out one or more of the following actions: (a) controlling the concentration of nitrogen and sulfur in the raw materials at each process stage, (b) promoting nitrogen removal from steel, (c) decreasing the time spent by the molten steel at each process stage and between each and subsequent process stages, and (d) preventing nitrogen pickup by the molten steel all along said process stages. Steel products made according to the Application comprise the following elements expressed in weight %: C≤0.05%, Si≤4.5%, Al≤2.0%; Mn≤2.0%; P≤0.20%; Ni≤0.200%, Cu≤0.200%; N≤0.0030%, Ni≤0.200%, S≤0.0035%.

Dependencies are inferred from the claim text.