Method for preparing liquid crystal polymer film, liquid crystal polymer film and application thereof

Abstract

A method for preparing a liquid crystal polymer film, comprising: (1) spinning a liquid crystal polymer into fibers, and maintaining the fibers for 0.1 hour to 36 hours at a temperature of 200° C. to 400° C. under a vacuum degree less than 500 Pa for later use; (2) weaving the fibers prepared in step (1) into cloth for later use; and (3) pressing the cloth prepared in step (2) into a film at a temperature of 200° C. to 400° C., and then stretching the film to obtain the liquid crystal polymer film. The liquid crystal polymer film prepared by the preparation method is good in mechanical property, and has a tensile strength that can exceed 170 MPa. The prepared liquid crystal polymer film is applied to a FPC, which makes the FPC have a dielectric constant less than 3, and a small dielectric loss tangent angle.