Fiber-reinforced molding material and molded article using same

Abstract

Provided is a fiber-reinforced molding material containing a thickening substance (A) containing a vinyl ester resin (a1), an unsaturated monomer (a2), a polyisocyanate (a3), and a polymerization initiator (a4) as essential raw materials and carbon fibers (B) with a fiber length of 2.5 mm to 50 mm. The thickening substance (A) satisfies conditions (1) to (3) below as measured with a rheometer. (1) The maximum value of the rate of change in viscosity in a temperature region lower than a temperature Xa indicating the lowest melt viscosity A is 100 Pa·s/° C. to 1,500 Pa·s/° C. (2) The maximum value of the rate of change in viscosity in a temperature region higher than or equal to the temperature Xa is 1,000 Pa·s/° C. to 10,000 Pa·s/° C. (3) The lowest melt viscosity A is 10 Pa·s to 1,000 Pa·s and the temperature Xa is 70° C. to 140° C.