Permeable, pourable concrete formulas and methods of use
AssigneePacific Interlock Pavers, Inc.
InventorsDean R. Tonder, Tim Donovan
Life of this patent
Estimating the term…
Abstract
A permeable, pourable concrete that has water permeability of on average about 1 inch per hour and compressive strength of an average of about 3000 psi, the permeable concrete comprising a mixture comprising blast-furnace slag, sand, gravel and Portland-type or equivalent cement, the concrete mixed with a predetermined ratio of water, poured into a predetermined form as desired, and set to harden until sufficiently strong.
Claims3
A method for producing a permeable concrete utilizing supplemental cementitious materials (SCMs) recovered from CO2 flue gases, having a water permeability in excess of 95-100 inches per hour and having an average compressive strength in excess of about 3000 psi, the method comprising the following steps;
- Combining (i) a base of 3 parts by weight of blast-furnace slag and 1 part by weight of sand, (ii) between about one fifth and one half parts by weight of ¼″ gravel, and (iii) between 15 and 21 parts by weight Portland-type or equivalent cement wherein up to 40% of the Portland-type or equivalent cement comprises SCMs formed by mineralization of CO2;
- Forming a concrete mix using a water ratio of between 15.25 gallons of water per yard of mixed concrete to 25 gallons of water per yard of mixed concrete;
- Pouring the mixed concrete into a predetermined form;
- and
- Setting the concrete for a sufficient period of time in order to achieve the compressive strength.
A method for reducing carbon emissions and producing a permeable concrete having a water permeability in excess of about 95-100 inches per hour and having an average compressive strength in excess of about 3000 psi, the method comprising the following steps:
- A. Forming supplemental cementitious materials (SCMs) comprising calcium carbonate recovered by mineralization of CO2;
- B. Combining (i) a base of 3 parts by weight of blast-furnace slag and 1 part by weight of sand, (ii) between about one fifth and one half part by weight of ¼″ gravel, and (iii) between 15 and 21 parts by weight Portland-type or equivalent cement wherein up to 40% of the Portland-type or equivalent cement comprises SCMs comprising calcium carbonate recovered by mineralization of CO2;
- C. Forming a concrete mix using a water ratio of between 15.25 gallons of water per yard of mixed concrete to 25 gallons of water per yard of mixed concrete;
- D. Pouring the mixed concrete into a predetermined form;
- and
- E. Setting the concrete for a sufficient period of time in order to achieve the compressive strength.
Dependencies are inferred from the claim text.