Stranded wire conductors and methods for manufacturing stranded wires
AssigneeHuzhou Jin Tai Conductor Technology Co., Ltd.
InventorXuebin Li
Life of this patent
Estimating the term…
Abstract
A stranded wire conductor and a method for manufacturing a stranded wire, wherein the stranded wire conductor is made of a plurality of composite wire monofilaments stranded together, each having a nickel-tantalum-tungsten core wire, a conductive alloy tube wrapped around an outside of the nickel-tantalum-tungsten core wire, and a plating disposed on an outside of the conductive alloy tube. By stranding the plurality of composite wire monofilaments together to form the stranded wire conductor, and the composite wire monofilament is made of the nickel-tantalum-tungsten core wire, the conductive alloy tube, and the plating, the stranded wire conductor can still maintain a high strength and conductivity when operating at a temperature in a range of 600° C. to 700° C.
Claims10
A stranded wire conductor that maintains high strength and high conductivity in a high temperature environment, wherein the stranded wire conductor is composed of a plurality of composite wire monofilaments stranded together, the composite wire monofilament includes a nickel-tantalum-tungsten core wire, a conductive alloy tube wrapped around an outside of the nickel-tantalum-tungsten core wire, and a plating provided on an outside of the conductive alloy tube;
- a composition of the nickel-tantalum-tungsten core wire includes 80% to 95% nickel, 0.5% to 10% tantalum, and 0.5% to 10% tungsten by weight, and a balance is trace impurities, an oxygen content of the nickel-tantalum-tungsten core wire is less than 9 ppm, a conductivity of the nickel-tantalum-tungsten core wire is in a range of 1% to 5%, and a tensile strength of the nickel-tantalum-tungsten core wire is not less than 1000 Mpa;
- the conductive alloy tube is a copper-based or silver-based alloy tube;
- a ratio of a cross-sectional area of a nickel-tantalum-tungsten alloy core wire in a composite wire to a total area of the composite wire is in a range of 20% to 40%;
- before stranding, the composite wire monofilament has a tensile strength being greater than 440 MPa at 20° C., a conductivity being greater than 70%, and an elongation being greater than 6%;
- and
- after stranding, the composite wire monofilament has a tensile strength being not less than 400 Mpa in a working environment at 600° C.
A method for manufacturing a stranded wire that maintains high strength and high conductivity in a high temperature environment, comprising following operations:
- S1, manufacturing a nickel-tantalum-tungsten core wire:
- 1.1, continuous casting:
- melting a nickel-tantalum-tungsten alloy in an oxygen-free environment followed by continuous casting to obtain a nickel-tantalum-tungsten alloy rod;
- 1.2, hot rolling:
- hot rolling the nickel-tantalum-tungsten alloy rod to reduce a diameter of the nickel-tantalum-tungsten alloy rod and refine grains of the of the nickel-tantalum-tungsten alloy rod;
- 1.3, wire drawing:
- performing a wire drawing process on a hot-rolled nickel-tantalum-tungsten alloy rod to obtain a nickel-tantalum-tungsten alloy wire with a smaller diameter;
- 1.4, annealing:
- annealing the nickel-tantalum-tungsten alloy wire obtained after the wire drawing process;
- and
- 1.5. polishing and cleaning:
- polishing and cleaning a surface of the annealed nickel-tantalum-tungsten alloy wire to obtain a finished nickel-tantalum-tungsten core wire;
- S2, manufacturing a copper-magnesium alloy tube:
- 2.1, continuous casting:
- continuous casting in an oxygen-free environment to obtain a copper-magnesium alloy tube blank;
- 2.2, ring rolling:
- ring rolling the copper-magnesium alloy tube blank to reduce a diameter and wall thickness of the copper-magnesium alloy tube blank and refine grains of the copper-magnesium alloy tube blank to obtain a rolled tube;
- 2.3. drawing:
- drawing the copper-magnesium alloy tube blank after the ring rolling to further reduce a diameter and wall thickness of the copper-magnesium alloy tube blank after the ring rolling to obtain a drawn tube;
- 2.4. bright annealing:
- bright annealing the tube blank after the ring rolling;
- and
- 2.5. polishing and cleaning:
- polishing and cleaning an inner surface of the tube blank to obtain a finished copper-magnesium alloy tube;
- S3, manufacturing a composite wire:
- 3.1. pipe threading:
- inserting the nickel-tantalum-tungsten core wire obtained in step 1.5 into the copper-magnesium alloy tube obtained in step 2.4 to obtain an initial composite wire;
- 3.2. drawing:
- drawing the initial composite wire obtained in step 3.1 to make the nickel-tantalum-tungsten core wire fit closely with the copper-magnesium alloy tube;
- 3.3. bright annealing:
- bright annealing a product obtained in step 3.2;
- 3.4. repeating step 3.2 and step 3.3 in sequence, and a drawing deformation rate each time does not exceed 40%, until a composite wire with an outer diameter of 1 mm is obtained;
- 3.5. plating:
- performing a nickel-plating anti-corrosion processing on the composite wire obtained in step 3.4;
- 3.6. wire drawing:
- performing a wire drawing process on the composite wire after the platina to make a diameter of the composite wire to be 0.1 mm to obtain a composite wire monofilament;
- and
- 3.7. heat treatment:
- subjecting the composite wire monofilament to an inert gas protection heat treatment;
- S4, manufacturing a composite stranded wire
- 4.1. stranding:
- stranding a plurality of the composite wire monofilament obtained in step 3.7 to obtain the composite stranded wire;
- and
- 4.2. heat treatment:
- subjecting the composite stranded wire strand to an inert gas protection heat treatment.
Dependencies are inferred from the claim text.