Ferritic stainless steel having improved corrosion resistance, and manufacturing method therefor
AssigneePosco
InventorsKwang Min Kim, Kkoch Nim Oh, Dong-Hoon Kim
Life of this patent
Estimating the term…
Abstract
A ferritic stainless steel with improved corrosion resistance. The ferritic stainless steel with improved corrosion resistance according to an embodiment of the present disclosure includes, in percent (%) by weight of the entire composition, C: 0.02% or less (excluding 0), N: 0.02% or less (excluding 0), Si: 0.5% or less (excluding 0), Mn: 0.3% or less (excluding 0), Cr: 16 to 20%, Ni: 0.4% or less (excluding 0), the remainder of iron (Fe) and other inevitable impurities, and a Cr weight % content of a thickness region from a surface of a passivation film to 3 nm is 1.2 times or more than the Cr weight % content of the stainless base material.
Claims10
A ferritic stainless steel comprising:
- a stainless base material comprising, in percent (%) by weight of the entire composition,
- C:
- 0.02% or less (excluding 0),
- N:
- 0.02% or less (excluding 0),
- Si:
- 0.5% or less (excluding 0),
- Mn:
- 0.2% to 0.3%,
- Cr:
- 16% to 20%,
- Ni:
- 0.2% to 0.4%, and
- the remainder of iron (Fe) and inevitable impurities;
- and
- a passivation film formed on the stainless base material, and
- wherein a Cr weight % content of a thickness region from a surface of the passivation film to 3 nm is 1.2 times or more than the Cr weight % content of the stainless base material.