Liquid epoxy molding compound and preparation method thereof

Abstract

Disclosed is a liquid epoxy molding compound and a preparation method thereof; the liquid epoxy molding compound includes the following raw materials by mass fraction: an inorganic silicon filler: 83%-88%, a naphthalene-based epoxy resin: 5%-10%, an anhydride curing agent: 5%-10%, and an accelerator: 0.1%-0.5%, where the inorganic silicon filler with a particle size of less than 50 μm-100 μm accounts for 99%; the method includes premixing the naphthalene-based epoxy resin, the curing agent, the accelerator, and the inorganic silicon filler to obtain a mixture; and grinding the mixture to a target particle size, and then performing vacuum degassing to obtain the liquid epoxy molding compound. The small-particle silica is introduced to reduce the increase in length of the liquid epoxy molding compound at the unit temperature during the molding stage.