Article made from post consumer resin with smooth surface finish

A process comprising:

• providing pellets of a regrind material, the regrind material being a post-consumer recycle multilayer film (PCR multilayer film) having at least three layers of (i) a polyethylene layer, (ii) a polyamide layer, and (iii) a tie layer, the tie layer composed of maleic anhydride grafted substantially linear ethylene polymer (MAH-g-SLEP) having a Mw/Mn from 1.5 to less than 3.5 and a melt index from 0.3 g/10 min to less than 25 g/10 min as measured in accordance with ASTM D1238 (190° C./2.16 kg), the regrind material comprising
• from 82 wt % to 89.5 wt % polyethylene,
• from 10 wt % to 15 wt % polyamide, and
• from 0.5 wt % to 3.0 wt % MAH-g-SLEP;
• extruding the pellets to form an extrudate;
• molding the extrudate;
• and
• forming, with the extrudate, a molded article having a surface, the surface having a surface roughness value, Sa, less than 1000 nm and a root mean square roughness value, Sq, less than 1400 nm.