Metal wick material with hierarchical porous structures and its fabrication method

A method for fabricating a metal wick material with hierarchical porous structures, wherein the hierarchical porous structures are composed of different pore size ranges of large pores, medium pores and small pores,

• wherein pore sizes of the large pores are between 100 and 800 microns, pore sizes of the medium pores are between 30 and 80 microns, pore sizes of the small pores are between 1 and 10 microns;
• wherein the large pores are obtained by 3D printing, the medium pores are obtained by volatilizing a binder during a water bath heating process, and the small pores are composed of voids among metal powder particles after sintering;
• wherein the method comprises the following steps:
• Step 1:
• mixing the metal powder particles with the binder to prepare a powder feed;
• wherein particle sizes of the metal powder particles are less than or equal to 15 microns, a volume fraction of the binder in the powder feed is between 40% and 60%, wherein the binder comprises polyethylene glycol, polyoxymethylene and paraffin, the powder feed is a subsphaeroidal feed with a particle size in a range of 1-5 mm and is prepared by means of mixing, banburying and granulation;
• Step 2. printing on a powder extrusion 3D printing device according to a pre-designed three-dimensional net structure model with the powder feed obtained in Step 1, to obtain a printed green body;
• wherein a printing infill rate of the 3D printing is 40-80%, and a layer thickness is 0.1-0.4 mm;
• Step 3:
• subjecting the printed green body obtained in Step 2 to the water bath heating to remove the binder from the printed green body to obtain a treated green body;
• wherein a temperature of the water bath heating is 50-70° C. and heating time is 24-48 h;
• Step 4:
• drying the treated green body obtained in Step 3 to obtain a dried green body;
• and
• Step 5:
• sintering the dried green body obtained in Step 4 in a vacuum or reducing atmosphere to finally obtain the metal wick material with hierarchical porous structures.