Method for improving smooth running of casting of rare earth stainless steel using pulse current

A method for improving running of casting of rare earth stainless steel using pulse current, comprising the following steps:

• S1, after a molten steel enters a crystallizer from an immersion nozzle and solidifies into a billet, when a continuous casting pulling speed stabilizes, applying a pulse electric field to a molten steel in a tundish;
• S2, setting an initial pulse voltage, an initial pulse current, and an initial pulse frequency in accordance with rare earth element content in the molten steel;
• the rare earth element content in the molten steel is 100-500 ppm;
• the pulse voltage is 10-100 V;
• the pulse current is 20-500 A;
• the pulse frequency is 1,000-100,000 Hz;
• specific details of setting an initial pulse voltage, an initial pulse current, and an initial pulse frequency in accordance with rare earth element content in the molten steel are as follows:
• when the rare earth element content is 100-200 ppm, the initial pulse voltage is 10-20 V, the initial pulse current is 20-100 A, and the initial pulse frequency is 1,000-5,000 Hz;
• when the rare earth element content is 200-300 ppm, the initial pulse voltage is 20-40 V, the initial pulse current is 60-140 A, and the initial pulse frequency is 5,000-10,000 Hz;
• when the rare earth element content is 300-400 ppm, the initial pulse voltage is 40-60 V, the initial pulse current is 100-250 A, and the initial pulse frequency is 5,000-40,000 Hz;
• when the rare earth element content is 400-500 ppm, the initial pulse voltage is 60-100 V, the initial pulse current is 200-500 A, and the initial pulse frequency is 10,000-100,000 Hz;
• S3, according to a position change of a stopper rod during continuous casting, adjusting the pulse voltage, the pulse current and the pulse frequency in real-time until the continuous casting is complete, and then terminating the pulse electric field;
• the specific details of adjusting the pulse voltage, the pulse current, and the pulse frequency in real-time according to the position change of the stopper rod during continuous casting are as follows:
• when the rare earth element content in the molten steel is 100-300 ppm, increasing the pulse voltage, the pulse current, and the pulse frequency by 30-50% when the position of the stopper rod rises by more than 6 mm within 20 minutes;
• when the position of the stopper rod rises by more than 8 mm within 35 minutes, increasing the pulse voltage, the pulse current, and the pulse frequency all by 40-80%;
• when the rare earth element content in the molten steel is 300-400 ppm, increasing the pulse voltage, the pulse current, and the pulse frequency by 20-40% when the position of the stopper rod rises by more than 6 mm within 25 minutes;
• when the position of the stopper rod rises by more than 8 mm within 40 minutes, increasing the pulse voltage, the pulse current, and the pulse frequency all by 30-50%;
• when the rare earth element content in the molten steel is 400-500 ppm, increasing the pulse voltage, the pulse current, and the pulse frequency by 20% when the position of the stopper rod rises by more than 6 mm within 25 minutes;
• when the position of the stopper rod rises by 8 mm within 40 minutes, increasing the pulse voltage, the pulse current, and the pulse frequency to an upper parameter range.