A woven product, wherein the woven product is woven from one or more selected from the group consisting of a PET-covered yarn, a PA6-covered yarn, a PA66-covered yarn, a PPS-covered yarn, and an LCP-covered yarn, wherein
- each of the PET-covered yarn, the PA6-covered yarn, the PA66-covered yarn, the PPS-covered yarn, and the LCP-covered yarn comprises a skin layer and a core layer, wherein
- the skin layer comprises 20 wt % to 30 wt % of a powder mixture and 80 wt % to 70 wt % of a mixed-melt material;
- the core layer comprises 100 wt % of a core-layer filament;
- the powder mixture is composed of the following components:
- 20 wt % of a CNT, 35 wt % of a graphite powder, 25 wt % of a copper powder, and 20 wt % of a jade ore powder;
- the mixed-melt material comprises one or more from the group consisting of PET, PA 6, PA66, PPS, LCP, and PC;
- and
- the core-layer filament comprises one or more from the group consisting of PET, PA66, PPS, and LCP, and the core-layer filament is a solid filament;
- wherein the PET-covered yarn is obtained by mixing and melting the powder mixture and the PET used as the mixed-melt material to obtain a first resulting melt, subjecting the first resulting melt to an extrusion with a twin-screw extruder to form a first skin layer, and wrapping the core-layer filament with the first skin layer to obtain the PET-covered yarn;
- wherein the core-layer filament is one or two from the group consisting of PPS and LCP;
- wherein the PA6-covered yarn is obtained by mixing and melting the powder mixture and the PA6 to obtain a second resulting melt, subjecting the second resulting melt to the extrusion with the twin-screw extruder to form a second skin layer, and wrapping the core-layer filament with the second skin layer to obtain the PA6-covered yarn;
- wherein the PA66-covered yarn is obtained by mixing and melting the powder mixture and the PA66 used as the mixed-melt material to obtain a third resulting melt, subjecting the third resulting melt to the extrusion with the twin-screw extruder to form a third skin layer, and wrapping the core-layer filament with the third skin layer to obtain the PA66-covered yarn;
- wherein the core-layer filament is one or two from the group consisting of PPS and LCP;
- wherein the PPS-covered yarn is obtained by mixing and melting the powder mixture and the PPS used as the mixed-melt material to obtain a fourth resulting melt, subjecting the fourth resulting melt to the extrusion with the twin-screw extruder to form a fourth skin layer, and wrapping the core-layer filament with the fourth skin layer to obtain the PPS-covered yarn;
- wherein the core-layer filament is LCP;
- and
- wherein the LCP-covered yarn is obtained by mixing and melting the powder mixture and the LCP used as the mixed-melt material to obtain a fifth resulting melt, subjecting the fifth resulting melt to the extrusion with the twin-screw extruder to form a fifth skin layer, and wraps the core-layer filament with the fifth skin layer to obtain the LCP-covered yarn;
- wherein the core-layer filament is LCP.