US 12,098,450 B2Granted

Tracked undercarriage component, and method for producing the same

AssigneesKomatsu Ltd., Nippon Steel Corporation

InventorsEiji Amada, Kazuo Maeda, Naomi Kobayashi, Takashi Noda, Mamoru Hatano, Takafumi Amata, Yutaka Neishi, Kei Miyanishi, Ryoji Nishijima

Life of this patent

Estimating the term…

patentgrep

Loading patent…

Abstract

A track link which is a tracked undercarriage component is made of a steel having a specific component composition, and includes a high hardness portion having a hardness of HRC 57 or more and HRC 60 or less, and a low hardness portion. The high hardness portion includes a first matrix including a martensite phase and a residual austenite phase, and first nonmetallic particles dispersed in the first matrix and including at least one species selected from the group consisting of MnS, TiCN, and NbCN, and it does not include a M23C6 carbide. The low hardness portion includes a second matrix including a martensite phase, and second nonmetallic particles dispersed in the second matrix and including at least one species selected from the group consisting of MnS, TiCN, and NbCN, and it does not include a M23C6 carbide.

Claims10

Dependent claims

A tracked undercarriage component made of a steel consisting of

not less than 0.41 mass % and not more than 0.44 mass % C,
not less than 0.2 mass % and not more than 0.5 mass % Si,
not less than 0.2 mass % and not more than 1.5 mass % Mn,
not less than 0.0005 mass % and not more than 0.0050 mass % S,
not less than 0.6 mass % and not more than 2.0 mass % Ni,
not less than 0.7 mass % and not more than 1.5 mass % Cr,
not less than 0.1 mass % and not more than 0.6 mass % Mo,
not less than 0.02 mass % and not more than 0.03 mass % Nb,
not less than 0.015 mass % and not more than 0.03 mass % Ti,
not less than 0.0005 mass % and not more than 0.0030 mass % B,
not less than 20 mass ppm and not more than 60 mass ppm N, and
optionally at least one species selected from the group consisting of
not less than 0.05 mass % and not more than 0.20 mass % V,
not less than 0.01 mass % and not more than 0.15 mass % Zr, and
not less than 0.1 mass % and not more than 2.0 mass % Co,
with the balance consisting of iron and unavoidable impurities,
the tracked undercarriage component comprising:
a high hardness portion having a hardness of HRC 57 or more and HRC 60 or less;
and
a low hardness portion constituting a region other than the high hardness portion and having a lower hardness than the high hardness portion;
the high hardness portion including
a first matrix including a martensite phase and a residual austenite phase, and
first nonmetallic particles dispersed in the first matrix and including at least one species selected from the group consisting of MnS, TiCN, and NbCN,
the high hardness portion not including a carbide represented as M23C6 (where M represents the metallic elements constituting the steel),
the low hardness portion including
a second matrix including a martensite phase, and
second nonmetallic particles dispersed in the second matrix and including at least one species selected from the group consisting of MnS, TiCN, and NbCN,
the low hardness portion not including a carbide represented as M23C6 (where M represents the metallic elements constituting the steel), and
the high hardness portion having a Charpy impact value of 68 J/cm2 or greater.

26 more elements

A method for producing a tracked undercarriage component, comprising the steps of:

preparing a steel material made of a steel consisting of:
not less than 0.41 mass % and not more than 0.44 mass % C,
not less than 0.2 mass % and not more than 0.5 mass % Si,
not less than 0.2 mass % and not more than 1.5 mass % Mn,
not less than 0.0005 mass % and not more than 0.0050 mass % S,
not less than 0.6 mass % and not more than 2.0 mass % Ni,
not less than 0.7 mass % and not more than 1.5 mass % Cr,
not less than 0.1 mass % and not more than 0.6 mass % Mo,
not less than 0.02 mass % and not more than 0.03 mass % Nb,
not less than 0.015 mass % and not more than 0.03 mass % Ti,
not less than 0.0005 mass % and not more than 0.0030 mass % B,
not less than 20 mass ppm and not more than 60 mass ppm N, and
optionally at least one species selected from the group consisting of
not less than 0.05 mass % and not more than 0.20 mass % V,
not less than 0.01 mass % and not more than 0.15 mass % Zr, and
not less than 0.1 mass % and not more than 2.0 mass % Co with the balance consisting of iron and unavoidable impurities;
hot forging the steel material to obtain a formed body;
performing quenching treatment on an entirety of the formed body by cooling the formed body from a temperature not lower than 945° C. and not higher than 1050° C. to a temperature not higher than the Ms point of the steel and, thereafter, performing high temperature tempering treatment on the entirety of the formed body by heating the formed body to a temperature not lower than 570° C. and not higher than 620° C.;
and forming a high hardness portion within the formed body by partially cooling the formed body having undergone the high temperature tempering treatment from a temperature not lower than 900° C. to a temperature not higher than the Ms point of the steel and, thereafter, adjusting a hardness of the high hardness portion to be HRC 57 or more and HRC 60 or less by heating the high hardness portion to a temperature not lower than 150° C. and not higher than 200° C.

16 more elements