Acid wash of red mud (bauxite residue)
AssigneeWorcester Polytechnic Institute
InventorsHimanshu Tanvar, Brajendra Mishra
Life of this patent
Estimating the term…
Abstract
Bauxite residue recovery includes mixing a solution of hydrochloric acid (HCL) according to a predetermined concentration, and adding the HCL solution to a quantity of raw red mud recovered from industrial operations as waste material. The highly alkaline property of the bauxite residue, commonly known as red mud is at least partially neutralized from the HCL, and makes the resulting washed red mud more amenable to subsequent uses in various applications in fields such as construction, wastewater treatment, and metal recovery processes. The process recovers washed red mud from the red mud and HCL solution by filtering the raw red mud and HCL solution for generating a stream of leach liquor from the filtrate and the recovered washed red mud from the residue.
Claims9
A method for recovering and recycling bauxite residue to form magnetite, comprising:
- mixing an acid wash solution according to a predetermined concentration;
- neutralizing a quantity of bauxite residue recovered from industrial operations as waste material by combining and washing the bauxite residue with the acid wash solution;
- recovering neutralized bauxite residue from the bauxite residue and the acid wash solution, the neutralized bauxite residue having a pH<7.0;
- generating a leach solution including the neutralized bauxite residue and a leach agent, the leach agent having a concentration based on an iron content in the neutralized bauxite residue;
- forming a slurry from the leach solution and filtering the slurry to generate a leach liquor and a solid residue of washed bauxite residue;
- separating a leach liquor from the slurry;
- directing UV (ultraviolet light) at the leach liquor for photochemical reduction;
- precipitating the iron in a form of ferrous oxalate via photochemical reduction;
- filtering the ferrous oxalate to form a magnetite precursor;
- and
- decomposing the magnetite precursor in an inert atmosphere heated to around 500° C. for around 1 hour to form magnetite.
Dependencies are inferred from the claim text.