Laminated cermet tool material with surface self generated micro texture and its preparation method

A laminated metal-ceramic tool material with a self-generating micro-weave structure on a surface, comprising a tool base, the tool base with a 2.5D woven ceramic fiber reinforcement layer provided on upper and lower surfaces of the 2.5D woven ceramic fiber reinforcement layer having a thickness of 0.8 mm-1.2 mm, a self-generating micro-bump weave structure on the surface of the upper and lower of the surfaces of the 2.5D woven ceramic fiber reinforcement layer, a laminated metal-ceramic tool with the 2.5D woven ceramic fiber reinforcement layer and the self-generating micro-bump weave structure provided on both sides of the tool base to form the tool;

• the 2.5D woven ceramic fiber reinforcement layer, and the laminated metal-ceramic tool with the self-generating micro-weave structure, was obtained by the following steps:
• (1) adding polyethylene glycol to anhydrous ethanol, stirred magnetically at constant temperature in a water bath and cooled to room temperature to produce polyethylene glycol-anhydrous ethanol dispersion;
• (2) adding metal phases to titanium (Ti,W)C carbide powder to obtain a mixed powder, dispersing the mixed powder in anhydrous ethanol and mix well to obtain the mixture, adding the polyethylene glycol-anhydrous ethanol dispersion to the mixture and mechanically stir and ultrasonically disperse for 45-60 min respectively to produce a (Ti,W)C—Mo—Co—Ni composite solution, wherein the metal phase comprises Co, Ni and Mo;
• (3) ball-milling the (Ti,W)C—Mo—Co—Ni composite solution produced in step (2) under nitrogen-protected atmosphere for 48˜60 h to produce a ball-milled slurry;
• (4) vacuum drying and sieving the ball-milled slurry from step (3) to obtain the metal-ceramic composite powder;
• and
• (5) placing 2.5D woven ceramic fiber preforms with the cermet matrix powder from step (4) in a graphite mold and perform electrical discharge plasma sintering to produce the laminated cermet tool material with the self-generated micro-weave structure on the surface;
• when placed, the 2.5D woven ceramic fiber preform are located on the upper and lower surfaces of the cermet matrix powder, the 2.5D woven ceramic fiber preforms are obtained by weaving ceramic fibers, the ceramic fiber structure is a shallow cross bending joint structure, the fiber diameter is 8-15 μm, the monofilament diameter is 13.6 μm, the tensile strength is 2.8 GPa, the tensile modulus is 315.0 GPa, the fracture strain is 0.9% ceramic fibers of second generation SiC fibers with a fiber diameter of 10-15 μm;
• the discharge plasma sintering conditions are:
• sintering temperature 1350-1550° C., sintering pressure 30-35 MPa, heating rate 100-150° C./min, holding time 8-10 min.