Low gloss polyurethane coating compositions

Abstract

The present disclosure describes a low gloss polyurethane one component powder coating composition comprising 90 to 100 wt % of a resin system comprising a thermosetting resin, an isocyanate curing agent for reacting with the thermosetting resin, and a polycarbonate diol, wherein: the thermosetting resin comprises a first hydroxyl functional polyester resin (i) having a hydroxyl value of between 200 and 250 mgKOH/g and a second hydroxyl functional polyester resin (ii) having a hydroxyl value of between 20 and 40 mgKOH/g, the weight ratio of (i):(ii) ranges from 15:85 to 35:65, the isocyanate curing agent comprises at least one unblocked uretdione curing agent, the ratio of isocyanate groups of the curing agent to hydroxyl group of the thermosetting ranges between 0.8 to 1.2, and the total weight % of the polycarbonate diol in the coating composition ranges from 1 to 10 wt % based on the total weight of the coating composition.