Abstract
A bonded multilayer article including: (a) at least one first layer of a silicone-containing rubber substrate material bonded to (b) at least one second layer of a substrate material bondable to the first layer; wherein at least a portion of the surface of the first layer is activated for adhesion to increase the bond strength of the first layer to a second layer such that the bond strength of the first layer bonded to the second layer is increased; and a process for producing the above bonded multilayer article.
Claims10
A bonded multilayer article comprising:
- (a) at least one first layer of a silicone-containing rubber substrate material bonded to
- (b) at least one second layer of a substrate material bondable to the first layer, the at least one second layer of a substrate being a glass syntactic polyurethane;
- wherein the at least one first layer of a silicone-containing rubber substrate material comprises a high consistency silicone rubber having a gum with a Williams plasticity of from 30 mm/100 to 300 mm/100 as measured in accordance with ASTM D-926-08;
- wherein the first layer has at least a portion of the surface of the first layer activated by a flame treatment for adhering (bonding) the first layer to the second layer and for increasing the bond strength of the first layer to the second layer;
- and
- wherein the activated surface of the first layer, activated by a flame treatment, is bonded to the surface of the second layer, wherein the bond strength of the first layer bonded to the second layer is from 0.57 N/mm to 10.07 N/mm.
A process for producing a bonded multilayer article comprising the steps of:
- (a) applying at least one first layer of a cured silicone-containing rubber substrate material to at least one second layer of an uncured substrate material bondable to the first layer;
- wherein the at least one first layer of a silicone-containing rubber substrate material comprises a cured high consistency silicone rubber having a gum with a Williams plasticity of from 30 mm/100 to 300 mm/100 as measured in accordance with ASTM D-926-08;
- (b) flame treating at least a portion of the surface of the cured first layer to activate the surface of the cured first layer for bonding the first layer to the second layer and for increasing the bond strength of the first layer to the second layer, the second layer comprising a glass syntactic polyurethane;
- and
- (c) heating the multilayer article of step (b) at a temperature sufficient to cure the uncured second layer and sufficient to bond the first layer to the second layer to form a bonded multilayer article, wherein the bond strength of the first layer bonded to the second layer is from 0.57 N/mm to 10.07 N/mm.
A process for producing a bonded multilayer article comprising the steps of:
- (a) applying at least one first layer of an uncured silicone-containing rubber substrate material to at least one second layer of an uncured substrate material bondable to the first layer, the at least one second layer of a substrate material being a glass syntactic polyurethane;
- wherein the at least one first layer of a silicone-containing rubber substrate material comprises an uncured high consistency silicone rubber having a gum with a Williams plasticity of from 30 mm/100 to 300 mm/100 as measured in accordance with ASTM D-926-08;
- (b) flame treating at least a portion of the surface of the uncured first layer to activate the surface of the uncured first layer for adhering (bonding) the first layer to the second layer and for increasing the bond strength of the first layer to the second layer;
- and
- (c) heating the multilayer article of step (b) at a temperature sufficient to cure the uncured first layer and the uncured second layer and sufficient to bond the first layer to the second layer to form a bonded multilayer article, wherein the bond strength of the first layer bonded to the second layer is from 0.57 N/mm to 10.07 N/mm.