Preparation method of heat-resistant adhesive of silicon-boron-carbon-zirconium modified aluminum-zirconium phosphate for zirconium oxide ceramics

A preparation method of heat-resistant adhesive of silicon-boron-carbon-zirconium modified aluminum-zirconium phosphate for zirconium oxide ceramics, comprising:

• step 1, adding a concentrated phosphoric acid into a three-necked flask, and placing the three-necked flask in a thermostat water bath cauldron for heating at a constant temperature in a range of 70-80° C., followed by adding water in the three-necked flask to dilute the concentrated phosphoric acid in the three-necked flask to obtain a diluted phosphoric acid with a concentration of 50-70%;
• performing mechanical stirring on the diluted phosphoric acid at a rotation speed in a range of 250-350 revolutions per minute (r/min), and adding aluminum hydroxide into the diluted phosphoric acid during the performing mechanical stirring on the diluted phosphoric acid, to obtain a first mixed solution, a solid-liquid mass ratio of the aluminum hydroxide:the diluted phosphoric acid being in a range of 1:1.4-3.8;
• performing mechanical stirring on the first mixed solution at a rotation speed in a range of 500-900 r/min for 6-8 hours for reacting, to thereby obtain a first reacted mixture;
• and filtering the first reacted mixture to remove residues from the first reacted mixture to thereby obtain an aluminum phosphate solution in milky white;
• wherein an entire process of the reacting is performed under a condition of installing a condensation reflux device;
• step 2, transferring the aluminum phosphate solution obtained in step 1 into a magnetic driven reactor, performing stirring on the aluminum phosphate solution at a rotation speed in a range of 200-400 r/min, and adding zirconium hydroxide to the aluminum phosphate solution during the performing stirring on the aluminum phosphate solution, to obtain a second mixed solution, a molar ratio of zirconium in the zirconium hydroxide:aluminum in the aluminum phosphate solution being in a range of 1:1.8-3;
• sealing the second mixed solution in the magnetic driven reactor, and performing stirring on the second mixed solution at a rotation speed in a range of 200-400 r/min under a temperature of 80-120° C. for 12-18 hours for reacting, to thereby obtain a second reacted mixture;
• and filtering the second reacted mixture to remove residues from the second reacted mixture, to thereby obtain an adhesive base solution in milky white;
• step 3, mixing a zirconium n-propoxide solution with an anhydrous ethanol solution to obtain a third mixed solution, a molar ratio of the zirconium n-propoxide solution:the anhydrous ethanol solution being in a range of 1:7-11, and then adding acetylacetone solution to the third mixed solution at a molar ratio of zirconium n-propoxide in the zirconium n-propoxide solution:acetylacetone in the acetylacetone solution being in a range of 1:1.5-2, followed by stirring at a rotation speed in a range of 400-500 r/min for 40-50 hours to obtain a zirconium gel solution;
• step 4, mixing a silicon powder, a graphite powder, and a boron carbide powder at a mass ratio of the silicon powder:the graphite powder:the boron carbide powder in a range of 3-5:1-1.5:2-4 to obtain a mixed powder, then adding the mixed powder into the zirconium gel solution obtained in step 3 at a solid-liquid ratio of the mixed powder:the zirconium gel solution in a range of 1:10-15, followed by mechanical stirring at a rotation speed in a range of 500-700 r/min for 24-36 hours for reacting, to thereby obtain a third reacted mixture, placing the third reacted mixture in an oven for drying the third reacted mixture at a temperature of 80-90° ° C. to thereby obtain a dried solid;
• and grinding the dried solid to obtain a reacted powder in brownish black;
• step 5, compressing, by using a tablet press, the reacted powder obtained in step 4 to obtain a cake-like solid at a pressure in a range of 2-4 megapascals (MPa), and then placing the cake-like solid in a tube furnace protected by an argon gas for cracking the cake-like solid to thereby obtain a calcined solid, a flow rate of the argon gas being in a range of 6-10 cubic centimeters per minute (cc/min), a period for the cracking being in a range of 2-4 hours, a temperature for the cracking being in a range of 450-550° C.;
• and crushing and grounding the calcined solid to obtain a reactive silicon-boron-carbon-zirconium powder with a particle size corresponding to 200-300 meshes as an adhesive filler;
• and
• step 6, mixing the adhesive base solution obtained in step 2 with the adhesive filler obtained in step 5 at a mass ratio of the adhesive base solution:the adhesive filler in a range of 4:1-5:1 to obtain a mixture, and performing mechanical stirring on the mixture at a rotation speed in a range of 600-800 r/min for 8-12 hours, to thereby obtain the heat-resistant adhesive of silicon-boron-carbon-zirconium modified aluminum-zirconium phosphate.