# US 12,015,155 B2 · Compositions for forming a porous insulating layer, electrode for non-aqueous electrolyte rechargeable battery, rechargeable battery including the electrode and method of manufacturing the electrode

> Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt

- Number: US 12,015,155 B2
- Document ID: US12015155B2
- Status: Granted
- Kind: B2
- Application number: 16/779,193
- Filed: 2020-01-31
- Published: 2020-08-06
- Granted: 2024-06-18
- Earliest claimed: 2019-02-01
- Assignees: Samsung SDI Co., Ltd.
- Applicants: Samsung SDI Co., Ltd.
- Inventors: Tomoyuki Fukatani; Koji Hoshiba
- Web page: https://patentgrep.com/patent/US12015155B2

## CPC

- H01M 4/622: {being polymers}
- H01M 4/13: Electrodes for accumulators with non-aqueous electrolyte, e.g. for lithium-accumulators; Processes of manufacture thereof
- H01M 4/133: Electrodes based on carbonaceous material, e.g. graphite-intercalation compounds or CFx
- H01M 4/139: Processes of manufacture
- H01M 4/1393: of electrodes based on carbonaceous material, e.g. graphite-intercalation compounds or CFx
- H01M 4/366: {as layered products}
- H01M 4/587: for inserting or intercalating light metals
- H01M 10/0525: Rocking-chair batteries, i.e. batteries with lithium insertion or intercalation in both electrodes; Lithium-ion batteries
- H01M 10/0569: characterised by the solvents
- H01M 2004/027: {Negative electrodes}
- Y02E 60/10: Energy storage using batteries
- H01M: PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- Y02E: REDUCTION OF GREENHOUSE GAS [GHG] EMISSIONS, RELATED TO ENERGY GENERATION, TRANSMISSION OR DISTRIBUTION

## Abstract

A composition to form a porous insulating layer on an active material layer on a main surface of a current collector current collector is provided. The active material layer includes an active material to electrochemically intercalate and deintercalate lithium ions and an active material layer binder, the composition to form the porous insulating layer includes a solvent including an organic solvent, an insulating inorganic particle, and a binder, and the binder is a polymer obtained by polymerization of monomers including about 30 wt % to about 60 wt % of an aromatic vinyl compound, about 20 wt % to about 69 wt % of (meth)acrylic acid ester, about 5 wt % to about 35 wt % of (meth)acrylic acid ester including a hydroxy group or an ether group, and about 1 wt % to about 10 wt % of a vinyl compound including an acidic functional group, based on a total weight of the binder.

## Claims

### Claim 1

A composition to form a porous insulating layer on an active material layer on a main surface of a current collector,
wherein the active material layer comprises an active material to electrochemically intercalate and deintercalate lithium ions and an active material layer binder,
the composition to form the porous insulating layer comprises a solvent, an insulating inorganic particle, and a porous insulating layer binder, the solvent comprising an organic solvent, and
the porous insulating layer binder is a polymer obtained by polymerization of monomers selected from the group consisting of about 30 wt % to about 60 wt % of an aromatic vinyl compound, about 20 wt % to about 69 wt % of (meth)acrylic acid ester, about 5 wt % to about 35 wt % of (meth)acrylic acid ester comprising a hydroxy group or an ether group, and about 1 wt % to about 10 wt % of a vinyl compound comprising an acidic functional group, based on a total weight of the porous insulating layer binder,
wherein a distance between Hansen solubility parameters of the active material layer binder and the organic solvent is greater than or equal to about 8.0 MPa1/2.

### Claim 2 (depends on 1)

The corn position of claim 1, wherein a distance between Hansen solubility parameters of the active material and the organic solvent is greater than or equal to about 5.0 MPa1/2.

### Claim 3 (depends on 1)

The composition of claim 1, wherein the organic solvent has a distance (Ra) with respect to graphene of Hansen solubility parameter calculated utilizing Equation 1 of greater than or equal to about 5.0 MPa1/2:
Ra={4×(18.0−δD(solvent))2+(9.3−δP(solvent))2+(7.7−δH(solvent))2}1/2 Equation 1
wherein, in Equation 1, δD(solvent) MPa1/2 denotes a solubility parameter due to dispersion force of the organic solvent, δP(solvent) MPa1/2 denotes a solubility parameter due to polarity (dipole-dipole force) of the organic solvent, and δH(solvent) MPa1/2 denotes a solubility parameter due to hydrogen bonding forces of the organic solvent.

### Claim 4 (depends on 1)

The composition of claim 1, wherein a boiling point of the organic solvent at 1 atm is greater than or equal to about 160° C.

### Claim 5 (depends on 1)

The composition of claim 1, wherein the organic solvent comprises an alcohol-based compound.

### Claim 6 (depends on 1)

The composition of claim 1, wherein the composition to form the porous insulating layer further comprises a polyolefin-based polymer particle.

### Claim 7 (depends on 1)

An electrode for a non-aqueous electrolyte rechargeable battery, the electrode comprising:
a current collector,
an active material layer on a main surface of a current collector, and
a porous insulating layer on the active material layer, the porous insulating layer being formed of the composition to form the porous insulating layer of claim 1,
wherein the active material layer comprises an active material to electrochemically intercalate and deintercalate lithium ions and an active material layer binder.

### Claim 8 (depends on 7)

A non-aqueous electrolyte rechargeable battery comprising the electrode for the non-aqueous electrolyte rechargeable battery of claim 7.

### Claim 9

A method for manufacturing an electrode for a non-aqueous electrolyte rechargeable battery, the method comprising:
forming a porous insulating layer on an active material layer on a current collector, the porous insulating layer being formed utilizing a composition to form a porous insulating layer,
wherein the active material layer comprises an active material to electrochemically intercalate and deintercalate lithium ions and an active material layer binder,
the composition to form the porous insulating layer comprises a solvent comprising an organic solvent, an insulating inorganic particle, and a porous insulating layer binder, and
the porous insulating layer binder is a polymer obtained by polymerization of monomers selected from the group consisting of about 30 wt % to about 60 wt % of an aromatic vinyl compound, about 20 wt % to about 69 wt % of (meth)acrylic acid ester, about 5 wt % to about 35 wt % of (meth)acrylic acid ester comprising a hydroxy group or an ether group, and about 1 wt % to about 10 wt % of a vinyl compound comprising an acidic functional group, based on a total weight of the binder,
wherein a distance between Hansen solubility parameters of the active material layer binder and the organic solvent is greater than or equal to about 8.0 MPa1/2.

### Claim 10 (depends on 9)

The method of claim 9, wherein a distance between Hansen solubility parameters of the active material and the organic solvent is greater than or equal to about 5.0 MPa1/2.

### Claim 11 (depends on 9)

The method of claim 9, wherein the organic solvent has a distance (Ra) with respect to graphene of Hansen solubility parameter calculated utilizing Equation 1 of greater than or equal to about 5.0 MPa1/2:
Ra={4×(18.0−δD(solvent))2+(9.3−δP(solvent))2+(7.7−δH(solvent))2}1/2 Equation 1
wherein, in Equation 1, δD(solvent) MPa1/2 denotes a solubility parameter due to dispersion force of the organic solvent, δP(solvent) MPa1/2 denotes a solubility parameter due to polarity (dipole-dipole force) of the organic solvent, and δH(solvent) MPa1/2 denotes a solubility parameter due to hydrogen bonding forces of the organic solvent.

### Claim 12 (depends on 9)

The method of claim 9, wherein a boiling point of the organic solvent at 1 atm is greater than or equal to about 160° C.

### Claim 13 (depends on 9)

The method of claim 9, wherein the organic solvent comprises an alcohol-based compound.

### Claim 14 (depends on 9)

The method of claim 9, wherein the composition to form the porous insulating layer further comprises a polyolefin-based polymer particle.