# US 12,006,430 B2 · Fire-retardant resins and composite materials > Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt - Number: US 12,006,430 B2 - Document ID: US12006430B2 - Status: Granted - Kind: B2 - Application number: 17/261,892 - Filed: 2019-08-02 - Published: 2021-09-16 - Granted: 2024-06-11 - Earliest claimed: 2018-08-03 - Assignees: Gurit (UK) Ltd. - Applicants: Gurit (UK) Ltd. - Inventors: Laura-Jane Slade; Paul John Spencer; Amy Alexandra Ferris - Web page: https://patentgrep.com/patent/US12006430B2 ## CPC - C08L 63/00: Compositions of epoxy resins; Compositions of derivatives of epoxy resins - C08L 63/04: Epoxynovolacs - C08G 59/245: {aromatic} - C08G 59/36: together with mono-epoxy compounds - C08G 59/38: together with di-epoxy compounds - C08J 5/042: {with carbon fibres} - C08J 5/043: {with glass fibres} - C08J 5/046: {with synthetic macromolecular fibrous material} - C08J 5/10: characterised by the additives used in the polymer mixture - C08J 5/243: {using carbon fibres} - C08J 5/244: {using glass fibres} - C08J 5/249: {characterised by the additives used in the prepolymer mixture} - C08K 3/346: {Clay} - C08K 3/36: Silica - C08K 3/38: Boron-containing compounds - C08K 3/40: Glass - C08K 5/19: Quaternary ammonium compounds - C08K 5/21: Urea; Derivatives thereof, e.g. biuret - C08K 5/3155: {Dicyandiamide} - C08K 5/3445: Five-membered rings - C08K 5/34922: {Melamine; Derivatives thereof} - C08K 5/5313: Phosphinic compounds, e.g. R2=P(:O)OR' - C08K 5/5357: cyclic - C09J 7/35: Heat-activated - C09J 163/00: Adhesives based on epoxy resins; Adhesives based on derivatives of epoxy resins - C08J 2363/00: Characterised by the use of epoxy resins; Derivatives of epoxy resins - C08K 2003/322: {Ammonium phosphate} - C08K 2003/387: {Borates} - C08L 2201/02: Flame or fire retardant/resistant - C08L 2205/025: containing two or more polymers of the same hierarchy C08L, and differing only in parameters such as density, comonomer content, molecular weight, structure - C08L 2205/035: containing four or more polymers in a blend - C08L 2312/00: Crosslinking - C09J 2463/00: Presence of epoxy resin - C08L: COMPOSITIONS OF MACROMOLECULAR COMPOUNDS (compositions based on polymerisable monomers C08F, C08G; artificial filaments or fibres D01F; textile treating compositions D06) - C08G: MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS - C08J: WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H (working, e.g. shaping, of plastics B29) - C08K: Use of inorganic or non-macromolecular organic substances as compounding ingredients (paints, inks, varnishes, dyes, polishes, adhesives C09) - C09J: ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES (preparation of glue or gelatine C09H) ## Abstract An epoxide resin for the manufacture of a fibre-reinforced composite material having fire retardant properties and/or for use as an adhesive or hot-melt adhesive having fire retardant properties, the epoxide resin being halogen-free and phenolic resin-free, the epoxide resin having: A. a mixture of (i) at least one first non-halogenated multifunctional epoxide-containing resin which has an epoxide functionality of greater than 2 and (ii) at least one second non-halogenated multifunctional epoxide-containing resin which has an epoxide functionality of less than or equal to 2; B. at least one catalyst for curing the mixture of epoxide-containing resins to form a cured epoxy resin; and C. a mixture of first, second and third fire retardant additives for reacting together to form an intumescent char when the cured epoxy resin is exposed to a fire, wherein (i) the first fire retardant additive comprises a blowing agent for generating a non-combustible gas, (ii) the second fire retardant additive comprises an acid donor for decomposing to form a phosphoric acid when the cured epoxy resin is exposed to a fire, and (iii) the third fire retardant additive comprises at least one or both of (a) a ceramic or glass material and (b) a ceramic or glass material precursor to form a ceramic or glass material when the cured epoxy resin is exposed to a fire. ## Claims ### Claim 1 An epoxide resin for the manufacture of a fibre-reinforced composite material having fire retardant properties and/or for use as an adhesive or hot-melt adhesive having fire retardant properties, the epoxide resin being halogen-free and phenolic resin-free, the epoxide resin comprising: A. a mixture of (i) at least one first non-halogenated multifunctional epoxide-containing resin which has an epoxide functionality of greater than 2 and which is solid at 20° C., and (ii) at least one second non-halogenated multifunctional epoxide-containing resin which has an epoxide functionality of less than or equal to 2 and which is liquid at 20° C.; B. at least one catalyst for curing the mixture of epoxide-containing resins to form a cured epoxy resin; and C. a mixture of first, second and third fire retardant additives for reacting together to form an intumescent char when the cured epoxy resin is exposed to a fire, wherein (i) the first fire retardant additive comprises a blowing agent for generating a non-combustible gas, (ii) the second fire retardant additive comprises an acid donor for decomposing to form a phosphoric acid when the cured epoxy resin is exposed to a fire, wherein the second fire retardant additive comprises or consists of ammonium polyphosphate and the ammonium polyphosphate of the second fire retardant additive is present in a concentration of from 27 to 32.5 wt % based on the weight of the epoxide resin, and (iii) the third fire retardant additive comprises at least one or both of (a) a ceramic or glass material and (b) a ceramic or glass material precursor for to form a ceramic or glass material when the cured epoxy resin is exposed to a fire, wherein in the mixture of first, second and third fire retardant additives, the first, second and third fire retardant additives are present in a weight ratio of 1:6-6.5:1.3-1.7. ### Claim 2 (depends on 1) An epoxide resin according to claim 1 wherein the first fire retardant additive comprises or consists of melamine. ### Claim 3 (depends on 1) An epoxide resin according to claim 1 wherein the first fire retardant additive is present in a concentration of from 4.6 to 4.7 wt %, based on the weight of the epoxide resin. ### Claim 4 (depends on 1) An epoxide resin according to claim 1 wherein the ammonium polyphosphate of the second fire retardant additive is present in a concentration of from 28.5 to 32 wt %, based on the weight of the epoxide resin. ### Claim 5 (depends on 1) An epoxide resin according to claim 1 wherein the third fire retardant additive comprises or consists of at least one of, or a mixture of any two or more of, the following: (i) a salt of a divalent metal cation and an oxoanion; (ii) a salt of a trivalent metal and an oxoanion; (iii) a glass material in particulate form; or (iv) a clay or ceramic material in particulate form. ### Claim 6 (depends on 5) An epoxide resin according to claim 5 wherein the third fire retardant additive comprises or consists of a salt of a zinc or calcium cation and an oxoanion selected from borate, molybdate, phosphate, phosphite, hypophosphite and hydroxyl stannate, the third fire retardant additive comprises or consists of a salt of aluminium and an oxoanion selected from borate, molybdate, phosphate, phosphite, hypophosphite and hydroxyl stannate, or the third fire retardant additive comprises or consists of an aluminosilicate clay in particulate form. ### Claim 7 (depends on 1) An epoxide resin according to claim 1 wherein the third fire retardant additive is present in a concentration of from 6 to 8 wt %, or from 6.75 to 7.5 wt %, based on the weight of the epoxide resin. ### Claim 8 (depends on 1) An epoxide resin according to claim 1 wherein in the mixture of first, second and third fire retardant additives, the first, second and third fire retardant additives are present in a weight ratio of 1:6.1-6.4:1.5-1.6. ### Claim 9 (depends on 1) An epoxide resin according to claim 1 wherein in the mixture of first, second and third fire retardant additives, the second and third fire retardant additives are present in a weight ratio of greater than 4:1 to up to 4.5:1. ### Claim 10 (depends on 1) An epoxide resin according to claim 1 wherein component A, the mixture of epoxide-containing resins, and component C, the mixture of first, second and third fire retardant additives, are present in a weight ratio of 52-68:32-48, or a weight ratio of 56-62:38-44. ### Claim 11 (depends on 1) An epoxide resin according to claim 1 wherein component C, the mixture of first, second and third fire retardant additives, provides the epoxide resin with a phosphorus content of from 7 to 10.5 wt %, or from 8 to 9.25 wt %, based on based on the weight of the epoxide resin. ### Claim 12 (depends on 1) An epoxide resin according to claim 1 wherein component C, the mixture of first, second and third fire retardant additives, provides the epoxide resin with a nitrogen content of from 5.8 to 8.25 wt %, or from 7 to 7.5 wt %, based on based on the weight of the epoxide resin. ### Claim 13 (depends on 1) An epoxide resin according to claim 1 wherein component A in the epoxide-resin has a viscosity of from 1.5 to 15 Pa·s measured at a temperature of 85° C., measured using a viscometer sold under the trade name Brookfield CAP2000HT viscometer, with a cone number 3, a rotational velocity of 50 rpm, and for a period of 20 seconds, or from 2 to 10 Pa·s, from 7 to 10 Pa·s or from 2 to 7 Pa·s measured under those conditions. ### Claim 14 (depends on 1) An epoxide resin according to claim 1 wherein in component A, the mixture comprises from 20 to 40 wt % of the at least one first non-halogenated multifunctional epoxide-containing resin, and from 10 to 30 wt % of the at least one second non-halogenated multifunctional epoxide-containing resin, each wt % being based on the weight of the epoxide resin; and wherein in component A, the mixture optionally further comprises from 5 to 15 wt %, based on the weight of the epoxide resin, of at least one third epoxide-containing resin which is semi-solid at 20° C. ### Claim 15 (depends on 1) An epoxide resin according to claim 1 wherein in component A, the at least one first non-halogenated multifunctional epoxide-containing resin is present in a concentration of from 8 to 12 wt %, or from 9 to 11 wt %, based on the weight of the epoxide resin. ### Claim 16 (depends on 1) An epoxide resin according to claim 1 wherein in component A, the at least one first non-halogenated multifunctional epoxide-containing resin comprises or consists of a solid bisphenol-A epoxy novolac resin. ### Claim 17 (depends on 1) An epoxide resin according to claim 1 wherein in component A, the at least one second non-halogenated multifunctional epoxide-containing resin is present in a concentration of from 45 to 52 wt %, or from 47 to 50 wt %, based on the weight of the epoxide resin. ### Claim 18 (depends on 1) An epoxide resin according to claim 1 wherein in component A, the at least one second non-halogenated multifunctional epoxide-containing resin comprises or consists of a liquid bisphenol-A epoxy resin, the at least one first non-halogenated multifunctional epoxide-containing resin optionally comprises an epoxy novolac resin, and the mixture further comprises a solid bisphenol-A epoxy resin. ### Claim 19 (depends on 18) An epoxide resin according to claim 18 wherein in component A, the solid bisphenol-A epoxy resin is present in a concentration of from 22 to 26 wt %, the liquid bisphenol-A epoxy resin is present in a concentration of from 12 to 17 wt %, and when present the epoxy novolac resin is present in a concentration of from 8 to 12 wt %, each based on the weight of the epoxide resin. ### Claim 20 (depends on 19) An epoxide resin according to claim 19 wherein in component A, the solid bisphenol-A epoxy resin is present in a concentration of from 23 to 25 wt %, the liquid bisphenol-A epoxy resin is present in a concentration of from 13 to 15 wt %, and when present the epoxy novolac resin is present in a concentration of from 9 to 11 wt %, each based on the weight of the epoxide resin. ### Claim 21 (depends on 1) An epoxide resin according to claim 1 which is free of any elastomeric material or elastomeric toughening additive. ### Claim 22 (depends on 1) An epoxide resin according to claim 1 wherein the at least one catalyst comprises plural catalysts, each having a respective curing temperature range, and the plural temperature ranges overlap to provide a cumulative curing temperature range for the epoxide-containing resin. ### Claim 23 (depends on 1) An epoxide resin according to claim 1 wherein the at least one catalyst for curing the epoxide-containing resin comprises or consists of a dicyanamide-based catalyst. ### Claim 24 (depends on 1) An epoxide resin according to claim 1 which is free of any epoxide-containing molecule that has been chemically reacted with a phosphinic acid derivative or dihydro-oxa-phospha-phenanthrene-oxide (DOPO). ### Claim 25 (depends on 1) An epoxide resin according to claim 1 further comprising at least one accelerator for the at least one catalyst, wherein the accelerator comprises an imidazole-based accelerator and/or a urea-based accelerator. ### Claim 26 (depends on 1) An epoxide resin according to claim 1 further comprising at least one anti-settling agent, wherein the at least one anti-settling agent comprises silicon dioxide, or amorphous silicon dioxide, or hydrophobic fumed silica, and wherein the at least one anti-settling agent is present in an amount of from 0.5 to 1.5 wt % based on the weight of the epoxide resin. ### Claim 27 (depends on 1) A prepreg comprising the epoxide resin of claim 1 and a fibrous reinforcement, wherein the epoxide resin forms an epoxide resin matrix which at least partially impregnates the fibrous reinforcement. ### Claim 28 (depends on 27) A fibre-reinforced composite material produced from the prepreg of claim 27.