Metal cap and method for manufacturing same

A method for manufacturing a metal cap that comprises:

• a metal cap shell having a top plate portion, a skirt portion extending downwardly from the periphery of the top plate portion, a grip portion that further extends downwardly from a lower end of the skirt portion and that is used for unsealing, and a pair of weakened lines formed from the vicinity of a base of the grip portion to the lower end of the skirt portion and through an upper end of the skirt portion to the top plate portion;
• and an olefin resin liner via a coating film on the top plate portion inner surface of the metal cap shell, the method comprising:
• coating a masking agent on the top plate portion inner surface of the metal cap shell, at a position on which a non-adhesive portion that is non-adhesive or weakly adhesive to the olefin resin liner is to be formed;
• coating a coating composition containing an adhesive component in a base resin at positions where the non-adhesive portion and an adhesive portion are to be formed, without curing the masking agent;
• and
• curing the masking agent and the coating composition so as to form the coating film comprising the adhesive portion that is adhesive to the olefin resin liner and the non-adhesive portion that is non-adhesive or weakly adhesive to the olefin resin liner, the adhesive portion is formed at a position coated with the coating composition other than the position coated with the masking agent, and the non-adhesive portion is formed at a position coated with the masking agent, wherein
• the adhesive portion of the coating film is formed by positioning the adhesive component of the coating composition on the coating film surface, the non-adhesive portion of the coating film has a masking layer of the masking agent at a side facing the metal cap shell, and a sea-island structure is formed on the coating film surface corresponding to the masking layer in which the adhesive component of the coating composition is a dispersion phase and the base resin is a continuous phase,
• a coating amount of the masking agent is 1 to 25 mg/dm2,
• a coating amount of the coating composition is 25 to 45 mg/dm2,
• the coating amount of the coating composition is larger than the coating amount of the masking agent, and the masking layer is covered entirely or partly with the coating composition, and
• the dispersion phase in the sea-island structure is 4 to 18 area %.