A method for non-destructive inspection of steel, the method comprising:
- a preparation step comprising preparing a non-destructive inspection apparatus that includes (i) a variable frequency circuit that is capable of changing a frequency of alternating current and (ii) a coil that is capable of inducing an AC magnetic field in response to the alternating current;
- a placing step comprising placing an object under inspection so that the AC magnetic field induced by the coil penetrates into the object under inspection, the object under inspection being the steel which has been subjected to one or more surface treatments, the one or more surface treatments including a carburizing treatment and a shot peening treatment;
- an eddy current generating step comprising generating eddy current in the object under inspection by allowing the AC magnetic field to penetrate into the object under inspection;
- a frequency changing step comprising continuously changing a penetration depth of the AC magnetic field in the object under inspection by causing the variable frequency circuit to continuously change the frequency of the alternating current from a low frequency to a high frequency;
- an impedance calculating step comprising calculating a value of impedance at each penetration depth in the object under inspection on the basis of a potential difference between opposite ends of the coil and a value of electric current passing through the coil;
- and
- an evaluation step comprising evaluating a state of the one or more surface treatments of the object under inspection by (a) calculating a ratio between the value of impedance at each penetration depth in the object under inspection calculated in the impedance calculating step and a value of impedance at a corresponding penetration depth in the steel which has not been subjected to the one or more surface treatments and (b) identifying as one or more causes of a change in magnetic permeability of the object under inspection, in which a defect occurred in the carburizing treatment and the shot peening treatment, on the basis of the ratio thus calculated, wherein
- in the evaluation step, the state of the one or more surface treatments of the object under inspection is evaluated by carrying out a method of assessment as follow:
- in a case where a difference in the ratio between non-defective and defective materials is expected to occur in a wide range of the penetration depth in the object under inspection, a method of assessment (1) of whether or not a distribution of the ratio is within a threshold range is carried out;
- in a case where the difference in the ratio between non-defective and defective materials is expected to appear notably in a specific part of the penetration depth, a method of assessment (2) of whether or not the ratio at a specific penetration depth is within a threshold range is carried out;
- and
- in a case where evaluation using the method of assessment (1) and evaluation using the method of assessment (2) are both difficult, a method of assessment (3) of whether or not an integral of the ratio in a specific penetration, depth range is within a threshold range is carried out, and
- in the evaluation step, in a case where the magnetic permeability of the object under inspection has been determined to be greater than that of a non-defective material which is the steel having been subjected to the one or more surface treatments, it is determined that a defect occurred in the carburizing treatment, and in a case where the magnetic permeability of the object under inspection has been determined to be less than that of the non-defective material, it is determined that a defect occurred in the shot peening treatment.