# US 11,898,303 B2 · Surface-modified aramid fiber and preparation method therefor

> Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt

- Number: US 11,898,303 B2
- Document ID: US11898303B2
- Status: Granted
- Kind: B2
- Application number: 17/052,903
- Filed: 2018-05-10
- Published: 2021-07-22
- Granted: 2024-02-13
- Earliest claimed: 2018-05-04
- Assignees: Soochow University
- Applicants: Soochow University
- Inventors: Aijuan Gu; Hua Cai; Guozheng Liang; Li Yuan
- Web page: https://patentgrep.com/patent/US11898303B2

## CPC

- D06M 11/38: Oxides or hydroxides of elements of Groups 1 or 11 of the Periodic Table
- D06M 7/00: {Treating fibres, threads, yarns, fabrics, or fibrous goods made of other substances with subsequent freeing of the treated goods from the treating medium, e.g. swelling, e.g. polyolefins (D06M10/00 takes precedence; treating fibres or filaments made of glass, mineral -, or slag wool C03C; carbon fibres D01F11/10)}
- D06M 10/001: {Treatment with visible light, infrared or ultraviolet, X-rays}
- D06M 11/36: with oxides, hydroxides or mixed oxides; with salts derived from anions with an amphoteric element-oxygen bond
- D06M 11/45: Oxides or hydroxides of elements of Groups 3 or 13 of the Periodic Table; Aluminates
- D06M 11/80: with boron or compounds thereof, e.g. borides (with boranes or diboranes D06M11/01; with boron carbides D06M11/74)
- D06M 13/513: with at least one carbon-silicon bond
- D06M 15/3562: {containing nitrogen}
- D06M 15/61: Polyamines {polyimines}
- D06M 23/08: Processes in which the treating agent is applied in powder or granular form (adhesives for multi-layer textile fabrics D06M17/00)
- B82Y 40/00: Manufacture or treatment of nanostructures
- D06M 2101/36: Aromatic polyamides
- D06M: TREATMENT, NOT PROVIDED FOR ELSEWHERE IN CLASS D06, OF FIBRES, THREADS, YARNS, FABRICS, FEATHERS OR FIBROUS GOODS MADE FROM SUCH MATERIALS
- B82Y: SPECIFIC USES OR APPLICATIONS OF NANOSTRUCTURES; MEASUREMENT OR ANALYSIS OF NANOSTRUCTURES; MANUFACTURE OR TREATMENT OF NANOSTRUCTURES

## Abstract

The present invention relates to a surface-modified aramid fiber and a method for preparing the same. The method includes the following steps: modifying an aramid fiber having amino groups and carboxyl groups on the surface with siloxane γ-glycidoxypropyltrimethoxysilane to obtain a silicon methoxylated aramid fiber; reacting same with a cerium oxide coated with polydopamine modified chaotic boron nitride to obtain a surface-modified aramid fiber. The cerium oxide coated with polydopamine modified chaotic boron nitride has high ultraviolet absorption, and has extremely low catalytic activity, avoiding the damage to a fiber structure by photocatalysis during radiation, being an effective, safe and highly-efficient ultraviolet absorber. The surface-modified aramid fiber provided in the present invention has an ultraviolet-resistant function, high surface activity, good thermal performance, and better mechanical performance, providing excellent overall performance, and having higher utilization value. The method is simple and controllable, being suitable for large scale production.

## Claims

### Claim 1

A method for preparing a surface-modified aramid fiber, comprising the following steps:
(1) immersing a surface-cleaned aramid fiber in an alkali metal hydroxide alcohol solution having a mass concentration of 5.0 to 15.0%, and shaking and reacting at 65° C. for 5 hours to obtain an aramid fiber grafted with amino and carboxyl groups on a surface thereof;
(2) immersing the aramid fiber grafted with amino and carboxyl groups in an organic solvent containing γ-glycidoxypropyltrimethoxysilane under an inert gas atmosphere, and reacting at 70° C. for 12 hours to obtain a silicon methoxylated aramid fiber;
(3) dissolving a cerium salt and an inorganic base in water, stirring for 35 minutes, adding hydrogen peroxide to obtain a suspension, adjusting a pH of the suspension to 12, reacting at 40° C. for 12 hours, washing and filtering, drying, calcining at 700° C. for 2 hours to obtain a nano-cerium oxide; dispersing the nano-cerium oxide, a boron source and a nitrogen-containing compound in a mixed solution of ethanol and water, ultrasonically stirring for 1 hour, steaming and drying, calcining at 950° C. for 5 hours under a nitrogen source gas to obtain cerium oxide particles coated with boron nitride;
(4) adding the cerium oxide particles coated with boron nitride and dopamine hydrochloride to a buffer having a pH of 8.5, and stirring at room temperature for 6 hours; filtering, washing, and drying to obtain a cerium oxide coated with polydopamine modified boron nitride;
(5) immersing the silicon methoxylated aramid fiber in an aqueous solution of the cerium oxide coated with polydopamine modified boron nitride, and shaking at 60° C. for 6 hours; washing and drying to obtain the surface modified aramid fiber,
wherein the aramid fiber is a para-aramid fiber or a meta-aramid fiber; the alkali metal hydroxide is sodium hydroxide; the inorganic base is sodium hydroxide; the inert gas is nitrogen gas; the organic solvent is ethanol; the cerium salt is cerium chloride; the boron source is boric acid; the nitrogen-containing compound is urea; the nitrogen source gas is nitrogen; and the buffer is Tris-HCl.

### Claim 2 (depends on 1)

The method for preparing the surface-modified aramid fiber according to claim 1, wherein an aramid fiber is sequentially immersed in acetone, petroleum ether and deionized water, each for 2 to 4 hours, and then washed and dried to obtain the surface-cleaned aramid fiber.

### Claim 3 (depends on 1)

The method for preparing the surface-modified aramid fiber according to claim 1, wherein a mass ratio of the aramid fiber grafted with amino and carboxyl groups, the γ-glycidyloxypropyltrimethoxysilane, and the organic solvent is 1:(100-200):(150-350); a mass ratio of the nano-cerium oxide, the boron source, the nitrogen-containing compound is 100:(30-50):(60-120); a mass ratio of the silicon methoxylated aramid fiber and the polydopamine-modified boron nitride coated cerium oxide is 1:(2-9); and a mass ratio of the cerium salt and the inorganic base is 100:(20-50).

### Claim 4 (depends on 1)

The surface-modified aramid fiber prepared by the method according to claim 1.