Organic polymer having asymmetric structure and use thereof as photoelectric materials
AssigneeChina Three Gorges Corporation
InventorDongxue Liu
Life of this patent
Estimating the term…
Abstract
An organic polymer having an asymmetric structure, a preparation method thereof and a use as a photoelectric material thereof, where the organic polymer with an asymmetric structure is obtained by polymerization after performing Stille coupling reaction between an electron-donating unit D and an electron-withdrawing unit A in the presence of a solvent and a catalyst. The compound of the present application has good heat stability, controllable absorption level, and is suitable for the preparation of hole transport materials of high-performance perovskite solar cells with high efficiency, flexibility, good stability and a large area as well as donor materials of organic solar cells.
Claims1
A preparation method of an asymmetric organic polymer, comprising:
- dissolving, in a 25 mL three-necked bottle, 80 mg of compound 8 and 137 mg of compound 9 in a mixture of 4.5 mL of toluene and 0.5 mL of N, N-dimethylformamide, bubble with nitrogen for 15 minutes;
- adding 5.17 mg of Pd2 (dba) 3 and p-(o-tol) 6 mg;
- heating and refluxing for 4 hours to produce a solution;
- stopping the heating immediately after the solution is viscous;
- cooling the solution, and loading the solution into 100 mL of anhydrous methanol for sedimentation;
- filtering by suction;
- using a Soxhlet extractor for purification;
- and
- using column chromatography for secondary purification to obtain 100.1 g of blue-black solid, wherein the reaction formula is as follows: