Amorphous metal oxide semiconductor layer and semiconductor device

A method for producing a semiconductor device having an amorphous metal oxide semiconductor layer, the amorphous metal oxide semiconductor layer produced through a method comprising:

• applying a precursor composition for forming an amorphous metal oxide semiconductor layer to form a precursor film, and
• firing the film at a temperature of 150° C. or higher and lower than 300° C.;
• wherein
• the precursor composition comprises a metal salt, a primary amide, and a waterbased solution,
• the metal salt is at least one inorganic acid salt selected from the group consisting of nitrate salts of In, Sn, Zn, and Ga,
• the primary amide is at least one species selected from the group consisting of acetamide, acetylurea, acrylamide, adipamide, acetaldehyde, semicarbazone, azodicarbonamide, 4-amino-2,3,5,6-tetrafluorobenzamide, β-alaninamide hydrochloride, L-alaninamide hydrochloride, benzamide, benzylurea, biurea, biuret, butylamide, 3-bromopropionamide, butylurea, 3,5-bis(trifluoromethyl)benzamide, tert-butyl carbamate, hexanamide, ammonium carbamate, ethyl carbamate, 2-chloroacetamide, (2-chloroethyl)urea, crotonamide, 2-cyanoactamide, butyl carbamate, isopropyl carbamate, methyl carbamate, cyanoacetylurea, cyclopropanecarboxamide, cyclohexylurea, 2,2-dichloroacetamide, dicyandiamidine phosphate, guanylurea sulfate, 1,1-dimethylurea, 2,2-dimethoxypropyonamide, ethylurea, fluoroacetamide, formamide, fumaramide, glycinamide hydrochloride, hydroxyurea, hydantoic acid, 2-hydroxyethylurea, heptafluorobutylamide, 2-hydroxyisobutylamide, isobutylamide, lactamide, maleamide, malonamide, 1-methylurea, nitrourea, oxamic acid, ethyl oxamate, oxamide, oxamic 39 hydrazide, butyl oxamate, phenylurea, phthalamide, propionamide, pivalacetamide, pentafluorobenzamide, pentafluoropropionamide, semicarbazide hydrochloride, succinamide, trichloroacetamide, trifluoroacetamide, urea nitrate, and valeramide,
• the waterbased solution contains water in an amount of 50 mass % or more,
• the precursor composition contains the primary amide in an amount of 5 to 50 mass % with respect to the amount of the metal salt,
• the precursor composition is a solution having a pH of 1 to 3, and
• the at least one inorganic acid salt is selected such that the amorphous metal oxide of the amorphous metal oxide semiconductor layer that is formed upon firing the precursor composition is at least one species selected from the group consisting of indium gallium zinc oxide, indium tin oxide, and indium zinc oxide.