AssigneeAdeka Corporation
InventorsNaoto Ueda, Kazukiyo Nomura
Life of this patent
Estimating the term…
Abstract
Disclosed is an acrylic resin composition that has excellent weather resistance and can be stably produced at high temperatures. Specifically, disclosed is an acrylic resin composition including, with respect to 100 parts by mass of an acrylic resin, from 0.1 to 8 parts by mass of a triazine-based UV absorber including 2-(4,6-diphenyl-1,3,5-triazin-2-yl)-5-[2-(2-ethylhexanoyloxy)ethoxy]phenol, wherein the acrylic resin used is an acrylic resin including at least 80 wt % of methyl methacrylate as a monomer component, and having a glass transition temperature of at least 80° C.
Claims3
A molded article obtained by melting and mixing/kneading an acrylic resin composition at a temperature of about 250° C.,
- wherein the acrylic resin composition comprises, with respect to 100 parts by mass of an acrylic resin, from 1 to 5 parts by mass of a triazine-based UV absorber consisting of 2-(4,6-diphenyl-1,3,5-triazin-2-yl)-5-[2-(2-ethylhexanoyloxy)ethoxy]phenol,
- wherein the acrylic resin consists of methyl methacrylate and optionally butyl methacrylate as monomer components, a blending amount of methyl methacrylate being 80 wt % or more, and a blending amount of butyl methacrylate being 20 wt % or less,
- wherein the acrylic resin has a glass transition temperature of from 82° C. to 105° C., and
- wherein the molecular weight of the acrylic resin is 87,000 to 119,000 in terms of mass average molecular weight.
A laminate in which a surface of a support material is covered by a thermoplastic resin layer having a thickness of from 30 to 300 μm,
- wherein the thermoplastic resin layer is formed by melting and mixing/kneading an acrylic resin composition at a temperature of about 250° C.,
- wherein the acrylic resin composition comprises, with respect to 100 parts by mass of an acrylic resin, from 1 to 5 parts by mass of a triazine-based UV absorber consisting of 2-(4,6-diphenyl-1,3,5-triazin-2-yl)-5-[2-(2-ethylhexanoyloxy)ethoxy]phenol,
- wherein the acrylic resin consists of methyl methacrylate and optionally butyl methacrylate as monomer components, a blending amount of methyl methacrylate being 80 wt % or more, and a blending amount of butyl methacrylate being 20 wt % or less,
- wherein the acrylic resin has a glass transition temperature of from 82° C. to 105° C., and
- wherein the molecular weight of the acrylic resin is 87,000 to 119,000 in terms of mass average molecular weight.
Dependencies are inferred from the claim text.