Method for binder additive manufacturing
AssigneeK.L. Chemicals Co., Ltd.
InventorsChien-Szu Huang, Ting-Chi Lai
Life of this patent
Estimating the term…
Abstract
A method for additive manufacturing is provided, including: mixing a hardener with a sand material, so that the hardener is evenly coated on a surface of the sand material, and then spraying a binder through a nozzle, reacting the binder sprayed through the nozzle with the surface of the sand material evenly coated with the hardener to harden a sand mold. Therefore, the problem of nozzle clogging may be overcome, and a solid with a particle size of less than 0.6 μm may be obtained by the additive manufacturing. In addition, the hardening speed can be adjusted according to the size of the sand mold. Compared with a general sand mold product, the hardening speed may be increased and the storage life of the binder may be prolonged when the sand mold has a large size.
Claims11
A method for additive manufacturing, comprising the following steps:
- stirring 1350-1650 parts by weight of furfuryl alcohol, 2-5 parts by weight of an acid catalyst, 120-180 parts by weight of a phenolic compound, and 60-90 parts by weight of polyoxymethylene to form a mixture of a binder, heating up to 120-150° C. and reacting for 1-2 h, then dehydrating at 85° C. or below, cooling down to 45° C. or below, and adding 5-10 parts by weight of a coupling agent, to obtain the binder;
- mixing p-toluenesulfonic acid with pure water in a ratio of 70-80 parts by weight to 20-30 parts by weight to form a mixture of the p-toluenesulfonic acid and the pure water, mixing phosphoric acid with the mixture of the p-toluenesulfonic acid and the pure water in a ratio of 90-100 parts by weight to 3-7 parts by weight, heating the obtained mixture of the phosphoric acid and the mixture of the p-toluenesulfonic acid and the pure water to 60-80° C., and stirring for 1-3 h, to obtain a hardener;
- mixing the hardener with a sand material in a mass ratio of 0.1-1.0% of the hardener to the sand material, heating at a high temperature of 100-110° C. for mixing, and drying, thereby coating the hardener evenly on a surface of the sand material, and then spraying the binder through a nozzle, with a mass ratio of the binder to the sand material being 0.5-2.5%;
- reacting the binder sprayed through the nozzle with the surface of the sand material evenly coated with the hardener to harden a sand mold.
A method for producing a binder for additive manufacturing, comprising the following steps:
- stirring 1350-1650 parts by weight of furfuryl alcohol, 2-5 parts by weight of an acid catalyst, 120-180 parts by weight of a phenolic compound, and 60-90 parts by weight of polyoxymethylene to form a mixture of a binder, heating up to 120-150° C. and reacting for 1-2 h, then dehydrating at 85° C. or below, cooling down to 45° C. or below, and adding 5-10 parts by weight of a coupling agent, to obtain the binder.
A method for additive manufacturing with a basic phenolic resin binder, comprising the following steps:
- stirring 1350-1650 parts by weight of furfuryl alcohol, 2-5 parts by weight of an acid catalyst, 120-180 parts by weight of a phenolic compound, and 60-90 parts by weight of polyoxymethylene to form a mixture of a binder, heating up to 120-150° C. and reacting for 1-2 h, then dehydrating at 85° C. or below, cooling down to 45° C. or below, and adding 5-10 parts by weight of a coupling agent and 5-20 parts by weight of basic phenolic resin, to obtain the binder;
- mixing p-toluenesulfonic acid with pure water in a ratio of 70-80 parts by weight to 20-30 parts by weight to form a mixture of the p-toluenesulfonic acid and the pure water, mixing phosphoric acid with the mixture of the p-toluenesulfonic acid and the pure water in a ratio of 90-100 parts by weight to 3-7 parts by weight, heating the obtained mixture of the phosphoric acid and the mixture of the p-toluenesulfonic acid and the pure water to 60-80° C., and stirring for 1-3 h, to obtain a hardener;
- mixing the hardener with a sand material in a mass ratio of 0.1-1.0% of the hardener to the sand material, heating at a high temperature of 100-110° C. for mixing, and drying, thereby coating the hardener evenly on a surface of the sand material, and then spraying the binder through a nozzle, with a mass ratio of the binder to the sand material being 0.5-2.5%;
- reacting the binder sprayed through the nozzle with the surface of the sand material evenly coated with the hardener to harden a sand mold.
Dependencies are inferred from the claim text.