Fiber-reinforced molded article and method of producing same

A method of producing a fiber-reinforced shaped article, wherein a resin-impregnated fiber base material in which a reinforcing fiber bundle aggregate formed of converged reinforcing fiber bundles is impregnated with an epoxy resin composition is passed through a pultrusion region and simultaneously the epoxy resin composition is heat-cured, whereby the resin-impregnated fiber base material is pultruded into a prescribed shape,

• wherein in the pultrusion region, at least a pultrusion die having an inlet part and an outlet part, and an after-cure furnace are arranged,
• in the pultrusion region, a process in which the resin-impregnated fiber base material is introduced from the inlet part of the pultrusion die, passed through the inside of the die, pulled out from the outlet part of the die, and then passed through the after-cure furnace is carried out, and
• conditions (i) to (v) are satisfied in the pultrusion region:
• (i) Formulae (1) to (3) are satisfied where a pultrusion die temperature is denoted by Tp (° C.) and an in-die residence time calculated by dividing a path length of the resin-impregnated fiber base material in the die defined as die path length (m) by a shaping speed (m/min) is denoted by H (min),
• 230−100H≤Tp≤252−80H (1)
• 180≤Tp≤245 (2)
• 0.1≤H≤0.9 (3);
• (ii) the epoxy resin composition is kept in a liquid state at the inlet part of the pultrusion die;
• (iii) the epoxy resin composition transitions from a liquid state to a gelled state in the die;
• (iv) the epoxy resin composition maintains a gelled state with a degree of cure of 33 to 80% at the die outlet part;
• (v) the epoxy resin composition is in a cured state with a degree of cure of 95% or more in the after-cure furnace,
• wherein the epoxy resin composition contains at least components [A], [B], [C], and [D], and
• a quantity of [A] is 60 to 100 parts by mass per 100 parts by mass of all epoxy resin contained in the epoxy resin composition:
• [A]:
• aminophenol epoxy resin;
• [B]:
• two acid anhydrides of
• [B1]:
• acid anhydride having a nadic anhydride structure, and
• [B2]:
• acid anhydride having a hydrogenated structure of phthalic anhydride;
• [C]:
• at least one filler having a Mohs hardness of 3 or less, selected from the group consisting of a silicon compound, a magnesium compound, a calcium compound, an aluminum compound, and inorganic carbon;
• [D]:
• a release agent.