Abstract
An aluminum magnesium alloy with reduced Samson phase at grain boundaries made from the method of providing aluminum in a container, adding boron to the container, providing an inert atmosphere, arc-melting the aluminum and the boron, and mixing the aluminum and the boron in the container to form an alloy mixture. A method of suppressing the Samson phase, Al3Mg2, at grain boundaries in Aluminum, comprising providing aluminum in a container, adding boron to the container, providing an inert atmosphere, arc-melting the aluminum and the boron, and mixing the aluminum and the boron in the container to form an alloy mixture.
Claims2
An aluminum-magnesium-manganese-iron-copper-chromium-titanium-silicon alloy comprising boron with reduced or no Samson phase, Al3Mg2, at grain boundaries in aluminum, made from the method of:
- providing aluminum in a container;
- adding boron to the container;
- providing an inert atmosphere;
- arc-melting the aluminum and the boron;
- mixing the aluminum and the boron in the container to form an alloy mixture;
- wherein the aluminum is Al-5083;
- wherein the boron reduces supersaturation of magnesium;
- wherein the boron traps the magnesium in a solid solution as AlMgB2 phase;
- further comprising the steps of
- adding copper to the container prior to the step of providing an the inert atmosphere;
- arc-melting the aluminum and the boron and the copper;
- mixing and homogenizing the aluminum, the boron and the copper in the container to form an alloy mixture with reduced or no Samson phase, Al3Mg2;
- wherein the step of mixing and homogenizing is at 500° C. for 2 hours;
- and
- annealing at 150° C. for about 190 hours.
An aluminum-magnesium-manganese-iron-copper-chromium-titanium-silicon alloy comprising boron with reduced or no Samson phase, Al3Mg2, at grain boundaries in aluminum, comprising:
- aluminum;
- boron;
- with reduced or no Samson phase, Al3Mg2,
- wherein the aluminum and the boron are arc-melted;
- wherein the aluminum and the boron are mixed to form an alloy mixture;
- wherein the aluminum is Al-5083 or Al-5456;
- wherein the boron reduces supersaturation of magnesium;
- wherein the boron traps the magnesium in a solid solution as AlMgB2 phase;
- copper and wherein the aluminum and the boron and the copper are arc-melted and undergo mixing and homogenizing to form an alloy mixture and annealed;
- wherein the mixing and homogenizing is at 500° C. for 2 hours;
- and
- wherein annealed at 150° C. for about 190 hours.