Multi-stage gas atomization preparation method of titanium alloy spherical powder for 3D printing technology

A multi-stage gas atomization preparation method of titanium alloy spherical powder for a 3D printing technology, comprising the following steps:

• step 1 (bar preparation and machining step):
• smelting a titanium alloy into a titanium alloy bar;
• and performing a mechanical machining to machine one end of the titanium alloy bar into a conical surface to prepare a titanium alloy electrode bar;
• step 2 (multi-stage gas atomization powder preparation step through vacuum induction):
• using a gas atomization equipment for operations, putting the titanium alloy electrode bar into a smelting chamber, clamping and fixing the titanium alloy electrode bar on an adding mechanism, placing the titanium alloy electrode bar into an induction coil, and making a cone angle at one end of the conical surface of the titanium alloy electrode bar align with a center of a gas atomization nozzle;
• closing a furnace door of the smelting chamber, performing an integral vacuum pumping on the gas atomization equipment, then charging an inert protective gas by the gas atomization nozzle;
• starting a motor, and controlling a rotation angle speed and a feeding speed of the titanium alloy electrode bar;
• turning on a smelting power supply, and continuously smelting a front end tip of the titanium alloy electrode bar to form continuous metal droplets, wherein a liquid flow of the metal droplets vertically falls into the center of the gas atomization nozzle;
• adjusting a gas atomization pressure, and achieving a multi-stage flexible control of inert gas, wherein a multi-stage gas atomization process is used for flexible control, when the metal droplets begin to drip, a gas atomization chamber, a valve of a tail discharge and a feeding mechanism are turned on, the feeding mechanism moves the titanium alloy electrode bar up and down, at a moment of the metal droplets dripping into the gas atomization chamber, the gas atomization nozzle spray the inert protective gas, so that the metal droplets are atomized and broken, and solidified into a titanium alloy spherical powder in the gas atomization chamber;
• wherein the multi-stage gas atomization process is set in sequence as below:
• (1) the gas atomization pressure is 5.5-6.5 MPa, and the feeding speed of the titanium alloy electrode bar is 0.4-0.6 mm/s;
• (2) the gas atomization pressure is 5-6 MPa, and the feeding speed of the titanium alloy electrode bar is 0.5-0.6 mm/s;
• (3) the gas atomization pressure is 5-6 MPa, and the feeding speed of the titanium alloy electrode bar is 0.6-0.7 mm/s;
• (4) the gas atomization pressure is 5-5.5 MPa, and the feeding speed of the titanium alloy electrode bar is 0.7-0.8 mm/s;
• (5) the gas atomization pressure is 5-5.5 MPa, and the feeding speed of the titanium alloy electrode bar is 0.8-0.9 mm/s;
• and (6) the gas atomization pressure is 4.5-5.5 MPa, and the feeding speed of the titanium alloy electrode bar is 0.9-1.0 mm/s;
• wherein time for each of the multi-stage gas atomization processes (1) to (6) is 10 seconds and the number of cycles of the multi-stage gas atomization processes (1) to (6) is 9-12;
• and after being cooled by a cooling water system, the titanium alloy spherical powder is transported into a cyclone separator through a powder conveying pipeline, and finally, reaches a powder collection tank to obtain the titanium alloy spherical powder;
• and
• step 3 (powder screening step):
• after the titanium alloy spherical powder prepared in the step 2 is cooled, performing a vibration screening according to requirements of different metal 3D printing technologies on particle size of the powder to obtain titanium alloy spherical powder for the different metal 3D printing technologies, and then performing a vacuum pumping molding for storage.