US 11,787,157 B2Granted
High heat dissipating thin film and method for manufacturing same
AssigneeSolueta
InventorsEui Hong Min, Sang Ho Cho, Buck Keun Choi
Life of this patent
Estimating the term…
Abstract
Provided is a high heat radiation thin film. The high heat radiation thin film may comprise a metal substrate, and a carbon layer which is disposed on the metal substrate and is thicker than 2.5 nm and thinner than 10 nm.
Claims14
A method of fabricating a high heat radiation thin film, the method comprising:
- preparing a copper substrate having a first surface and a second surface that is opposite the first surface;
- forming a preliminary carbon layer by providing carbon atoms onto the first surface of the copper substrate;
- rearranging the carbon atoms to form a first carbon layer that includes graphene, wherein the first carbon layer that includes graphene is formed on the first surface of the copper substrate, wherein the first carbon layer that includes graphene is formed by performing a heat treatment on the first copper substrate and the preliminary carbon layer at between 600° C. and 800° C., wherein the first carbon layer that includes graphene is formed under an oxygen-free and hydrogen-free atmosphere, and wherein the carbon layer that includes graphene has a thermal conductivity that is (i) higher than a thermal conductivity of the preliminary carbon layer and (ii) more than 409 W/mK;
- after forming the first carbon layer that includes graphene, forming a second carbon layer on the second surface of the copper substrate, wherein the second carbon layer is formed by preparing a carbon coating material comprising graphite powder and a binder, and applying the carbon coating material to the second surface of the copper substrate, and wherein the second carbon layer is thicker than the first carbon layer that includes graphene;
- and
- forming a pressure sensitive adhesion film on the second carbon layer,
- wherein a thickness of the first carbon layer that includes graphene is more than 2.5 nm and less than 10 nm.
4 more elements
A method of fabricating a high heat radiation thin film including a carbon material, the method comprising:
- preparing a first metal film comprising rolled copper, the first metal film having a first surface and a second surface that is opposite the first surface;
- forming a passivation film on the first surface of the first metal film, the passivation film comprising an alloy film of nickel and chromium (Cr);
- and
- forming a first carbon layer that includes graphene on the passivation film, wherein forming the first carbon layer comprises providing a preliminary layer of carbon ions onto the first surface of the first metal film having the passivation film formed thereon, and heat-treating the first metal film provided with the preliminary layer of carbon ions in an oxygen-free and hydrogen-free atmosphere at between 600° C. and 800° C.;
- after forming the first carbon layer, forming a second carbon layer on the second surface of the first metal film, wherein the second carbon layer is formed by preparing a carbon coating material comprising graphite powder and a binder, and coating the second surface of the first metal film with the carbon coating material, and wherein the second carbon layer is thicker than the first carbon layer;
- and
- forming a pressure sensitive adhesion film on the second carbon layer,
- wherein a thickness of the first carbon layer is more than 2.5 nm and less than 10 nm, and
- wherein a thermal conductivity of the first carbon layer is greater than 409 W/mK, and is also greater than a thermal conductivity of the preliminary layer of carbon ions.
6 more elements
A high heat radiation thin film including a carbon material, the high heat radiation thin film comprising:
- a first metal film comprising rolled copper, the first metal film having a first surface and a second surface that is opposite the first surface;
- a passivation film on the first surface of the first metal film, the passivation film comprising an alloy film of nickel and chromium (Cr);
- a first carbon layer formed on the passivation film, wherein the first carbon layer includes multiple layers of carbon atoms arranged in a honeycomb structure that collectively form a graphitic carbon layer having (i) a thickness that is more than 2.5 nm and less than 10 nm, and (ii) a thermal conductivity that is greater than or equal to 409 W/mK;
- a second carbon layer formed on the second surface of the first metal film, the second carbon layer comprising graphite powder and a binder, wherein the second carbon layer is thicker than the first carbon layer;
- and
- a pressure sensitive adhesion film formed on the second carbon layer.
3 more elements