Proton-conducting PBI membrane processing with enhanced performance and durability
AssigneeUniversity of South Carolina
InventorsLaura A. Murdock, Fei Huang, Brian C. Benicewicz
Life of this patent
Estimating the term…
Abstract
The current disclosure teaches one to achieve PBI membranes with high ionic conductivity and low mechanical creep for the first time. This is in contrast to previous teachings of PBI membrane fabrication methods, which yield PBIs with either high ionic conductivity and high mechanical creep or low ionic conductivity and low mechanical creep. The membranes produced according to the disclosed process provide doped membranes for applications in fuel cells and electrolysis devices such as electrochemical separation devices.
Claims15
A process for making a polybenzimidazole film comprising:
- forming a polymerization composition comprising a polyphosphoric acid, an aromatic or heteroaromatic tetraamino compound, and an aromatic or heteroaromatic polycarboxylic acid compound, wherein the aromatic or heteroaromatic carboxylic acid compound comprises an aromatic or heteroaromatic polycarboxylic acid or ester, anhydride, or acid chloride thereof and/or comprises an aromatic or heteroaromatic diaminocarboxylic acid;
- polymerizing the aromatic or heteroaromatic tetraamino compound with the aromatic or heteroaromatic carboxylic acid compound to form a polymer solution comprising a pol benzimidazole dissolved in the polyphosphoric acid;
- shaping the polymer solution to form a membrane precursor comprising the polymer solution;
- hydrolyzing at least a portion of the polyphosphoric acid to form phosphoric acid and water, upon which the membrane precursor forms a gel membrane comprising the polybenzimidazole, the gel membrane being a self-supporting membrane capable of incorporating a liquid content of about 60 wt. % or more without loss of structure;
- rinsing the gel membrane;
- restraining the gel membrane in an X-Y plane direction;
- drying the rinsed gel membrane as it is restrained to form a dried film;
- and
- immersing the dried film into an inorganic or organic acid bath.
A polybenzimidazole film comprising an inorganic or organic acid imbibed therein, the polybenzimidazole film having a thickness of 5 microns to 150 microns, wherein the polybenzimidazole film exhibits an ionic conductivity measured at 180° C. greater than 180 mS/cm and exhibits a steady state creep compliance of less than 5×10−6 Pa−1 when measured at 180° C.
Dependencies are inferred from the claim text.